- 密度 [g/cm3]: 1.48
- 吸水率 [%]: 6.6
- 缺口冲击强度: 4.6
- 弯曲强度 [MPa]: 135.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 | ||
| Water Absorption | 6.6 % | 6.6 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 23°C/50% R.H.; ISO 62 | ||
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 135 MPa | 19600 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.1 % | 3.1 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 8.53 GPa | 1240 ksi | 1mm/min; ISO 527 | ||
| Izod Impact, Notched (ISO) | 4.60 kJ/m² | 2.19 ft-lb/in² | ISO Test | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 201 °C | 394 °F | ISO 75 | ||
| Descriptive Properties | |||||
| Color | Ebony23227 | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||