- 密度 [g/cm3]: 1.48
- 吸水率 [%]: 2.2
- 缺口冲击强度: 0.4
- 弯曲强度 [MPa]: 130.0
- 热变形温度 [℃]: 214.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 | ||
| Water Absorption | 2.2 % | 2.2 % | 24 hour; ISO Test | ||
| 6.6 % | 6.6 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 23°C/50% R.H.; ISO 62 | ||
| Viscosity Test | 160 cm³/g | 160 cm³/g | Viscosity number | ||
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 130 MPa | 18900 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 130 MPa | 18900 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 2.7 % | 2.7 % | 5mm/min; ISO 527 | ||
| 2.7 % | 2.7 % | 0.2 in/min; ASTM Test | |||
| Tensile Modulus | 8.00 GPa | 1160 ksi | ASTM Test | ||
| 9.00 GPa | 1310 ksi | 1mm/min; ISO 527 | |||
| Izod Impact, Notched | 0.400 J/cm @Temperature -40.0 °C | 0.749 ft-lb/in @Temperature -40.0 °F | ASTM Test | ||
| 0.530 J/cm @Thickness 3.17 mm | 0.993 ft-lb/in @Thickness 0.125 in | ASTM Test | |||
| Charpy Impact, Notched | 0.390 J/cm² | 1.86 ft-lb/in² | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ISO 75 | ||
| 215 °C | 419 °F | ASTM Test | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C | 388 °F | ISO 75 | ||
| 200 °C | 392 °F | ASTM Test | |||
| Descriptive Properties | |||||
| Color | BK23220 | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||