- 密度 [g/cm3]: 1.48
- 吸水率 [%]: 2.2
- 缺口冲击强度: 1.34
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | dry; ISO 1183 | ||
| Water Absorption | 2.2 % | 2.2 % | 24 hour; ISO Test | ||
| 6.6 % | 6.6 % | beginning dry; ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | beginning dry (23°C/50% R.H.); ISO 62 | ||
| Viscosity Test | 160 cm³/g | 160 cm³/g | Viscosity number | ||
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 65.0 MPa | 9430 psi | 0.2 in/min; ASTM Test | ||
| Tensile Modulus | 5.00 GPa | 725 ksi | ASTM Test | ||
| Izod Impact, Notched | 1.34 J/cm @Thickness 3.17 mm | 2.51 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Descriptive Properties | |||||
| Color | BK23220 | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||