- 熔体流动速率 [g/10min]: 25.0
- 密度 [g/cm3]: 1.48
- 吸水率 [%]: 6.6
- 弯曲强度 [MPa]: 65.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | dry; ISO 1183 | ||
| Water Absorption | 6.6 % | 6.6 % | beginning dry; ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | beginning dry (23°C/50% R.H.); ISO 62 | ||
| Viscosity Test | 130 cm³/g | 130 cm³/g | Viscosity number | ||
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM Data; MD | ||
| Melt Flow | 25 g/10 min @Load 5.00 kg, Temperature 275 °C | 25 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 65.0 MPa | 9430 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 12 % | 12 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 5.00 GPa | 725 ksi | 1mm/min; ISO 527 | ||
| Tensile Creep Modulus, 1 hour | 2800 MPa | 406000 psi | ISO 899 | ||
| Tensile Creep Modulus, 1000 hours | 1850 MPa | 268000 psi | ISO 899 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 | ||
| Dielectric Constant | 6.2 @Frequency 1.00e+6 Hz | 6.2 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 0.020 @Frequency 100 Hz | 0.020 @Frequency 100 Hz | IEC 60250 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||