BASF Ultramid® HPN 9362 40% Mineral Filled PA6 (Conditioned)物性表参数

密度 [g/cm3]: 1.41
吸水率 [%]: 4.9
拉伸强度 [MPa]: 45.0
弯曲模量 [MPa]: 1.56

Physical Properties	Metric	English	Comments

Density	1.41 g/cc	0.0509 lb/in³	dry; ISO 1183
Water Absorption	4.9 %	4.9 %	beginning dry; ISO 62
Moisture Absorption at Equilibrium	1.4 %	1.4 %	beginning dry (23°C/50% R.H.); ISO 62
Linear Mold Shrinkage	0.010 cm/cm	0.010 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	45.0 MPa	6530 psi	0.2 in/min; ASTM Test
	20.0 MPa @Temperature 120 °C	2900 psi @Temperature 248 °F	ISO Data
	20.0 MPa @Temperature 120 °C	2900 psi @Temperature 248 °F	ASTM Test
	25.0 MPa @Temperature 80.0 °C	3630 psi @Temperature 176 °F	ASTM Test
	25.0 MPa @Temperature 80.0 °C	3630 psi @Temperature 176 °F	ISO Data
	95.0 MPa @Temperature -40.0 °C	13800 psi @Temperature -40.0 °F	ASTM Test
	95.0 MPa @Temperature -40.0 °C	13800 psi @Temperature -40.0 °F	ISO Data
Tensile Strength, Yield	45.0 MPa	6530 psi	2 in/min; ASTM Test
	45.0 MPa	6530 psi	50mm/min; ISO 527
	20.0 MPa @Temperature 120 °C	2900 psi @Temperature 248 °F	ISO Data
	20.0 MPa @Temperature 120 °C	2900 psi @Temperature 248 °F	ASTM Test
	25.0 MPa @Temperature 80.0 °C	3630 psi @Temperature 176 °F	ASTM Test
	25.0 MPa @Temperature 80.0 °C	3630 psi @Temperature 176 °F	ISO Data
	90.0 MPa @Temperature -40.0 °C	13100 psi @Temperature -40.0 °F	ASTM Test
	90.0 MPa @Temperature -40.0 °C	13100 psi @Temperature -40.0 °F	ISO Data
Elongation at Break	30 %	30 %	50mm/min, Nominal strain; ISO 527
	30 %	30 %	2 in/min; ASTM Test
	30 %	30 %	0.2 in/min; ASTM Test
	9.0 % @Temperature -40.0 °C	9.0 % @Temperature -40.0 °F	ASTM Test
	9.0 % @Temperature -40.0 °C	9.0 % @Temperature -40.0 °F	ISO Data
	25 % @Temperature 120 °C	25 % @Temperature 248 °F	ISO Data
	25 % @Temperature 120 °C	25 % @Temperature 248 °F	ASTM Test
	40 % @Temperature 80.0 °C	40 % @Temperature 176 °F	ASTM Test
	40 % @Temperature 80.0 °C	40 % @Temperature 176 °F	ISO Data
Elongation at Yield	27 %	27 %	2 in/min; ASTM Test
	27 %	27 %	50mm/min; ISO 527
	5.1 % @Temperature -40.0 °C	5.1 % @Temperature -40.0 °F	ISO Data
	5.1 % @Temperature -40.0 °C	5.1 % @Temperature -40.0 °F	ASTM Test
	25 % @Temperature 80.0 °C	25 % @Temperature 176 °F	ASTM Test
	25 % @Temperature 120 °C	25 % @Temperature 248 °F	ISO Data
	30 % @Temperature 80.0 °C	30 % @Temperature 176 °F	ISO Data
	30 % @Temperature 120 °C	30 % @Temperature 248 °F	ASTM Test
Tensile Modulus	2.90 GPa	421 ksi	1mm/min; ISO 527
	0.600 GPa @Temperature 120 °C	87.0 ksi @Temperature 248 °F	ISO Data
	0.860 GPa @Temperature 80.0 °C	125 ksi @Temperature 176 °F	ISO Data
	6.60 GPa @Temperature -40.0 °C	957 ksi @Temperature -40.0 °F	ISO Data
Flexural Strength	50.0 MPa	7250 psi	ASTM Test
	25.0 MPa @Temperature 120 °C	3630 psi @Temperature 248 °F	ASTM Test
	30.0 MPa @Temperature 93.0 °C	4350 psi @Temperature 199 °F	ASTM Test
	35.0 MPa @Temperature 65.0 °C	5080 psi @Temperature 149 °F	ASTM Test
	155 MPa @Temperature -40.0 °C	22500 psi @Temperature -40.0 °F	ASTM Test
Flexural Modulus	1.56 GPa	226 ksi	ASTM Test
	0.740 GPa @Temperature 120 °C	107 ksi @Temperature 248 °F	ASTM Test
	0.850 GPa @Temperature 93.0 °C	123 ksi @Temperature 199 °F	ASTM Test
	0.970 GPa @Temperature 65.0 °C	141 ksi @Temperature 149 °F	ASTM Test

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	10 K/min
	220 °C	428 °F	ASTM Test

Processing Properties	Metric	English	Comments
Melt Temperature	275 °C	527 °F	Injection molding
Mold Temperature	95.0 °C	203 °F	Injection molding

Descriptive Properties
Color	Natural
Commercial Status	Active America
Form	Pellets
Impact Modified	Yes
Primary Processing Technique	Injection Molding
Processing	Injection Molding
UL.UL-C	Yes