- 密度 [g/cm3]: 1.2
- 缺口冲击强度: 1.55
- 弯曲强度 [MPa]: 93.0
- 弯曲模量 [MPa]: 4.39
- 热变形温度 [℃]: 211.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 93.0 MPa | 13500 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 93.0 MPa | 13500 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 | ||
| Flexural Strength | 150 MPa | 21800 psi | ASTM Test | ||
| Flexural Modulus | 4.39 GPa | 637 ksi | ISO Data | ||
| 4.48 GPa | 650 ksi | ASTM Test | |||
| Izod Impact, Notched | 1.55 J/cm @Thickness 3.17 mm | 2.90 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Izod Impact, Notched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | ISO Test | ||
| 5.40 kJ/m² @Temperature -40.0 °C | 2.57 ft-lb/in² @Temperature -40.0 °F | ISO Test | |||
| Charpy Impact, Notched | 1.38 J/cm² | 6.57 ft-lb/in² | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 211 °C | 412 °F | ASTM Test | ||
| 211 °C | 412 °F | ISO 75 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ISO 75 | ||
| 190 °C | 374 °F | ASTM Test | |||
| Flammability, UL94 | HB @Thickness 1.00 mm | HB @Thickness 0.0394 in | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||||
| Descriptive Properties | |||||
| Color | BK-104 | ||||
| Commercial Status | Active America | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||
| UL.UL-C | Yes | ||||