- 密度 [g/cm3]: 1.45
- 缺口冲击强度: 11.6
- 弯曲强度 [MPa]: 190.0
- 弯曲模量 [MPa]: 10.74
- 热变形温度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 190 MPa | 27600 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 11.0 GPa | 1600 ksi | 1mm/min; ISO 527 | ||
| Flexural Modulus | 10.74 GPa | 1558 ksi | ISO Data | ||
| Izod Impact, Notched (ISO) | 11.6 kJ/m² | 5.52 ft-lb/in² | ISO Test | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75 | ||
| Descriptive Properties | |||||
| Color | BK-126 | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||