- 密度 [g/cm3]: 1.41
- 吸水率 [%]: 4.9
- 缺口冲击强度: 0.86
- 拉伸强度 [MPa]: 64.0
- 弯曲模量 [MPa]: 4.00
- 硬度: 119.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 | ||
| Water Absorption | 4.9 % | 4.9 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.4 % | 1.4 % | 23°C/50% R.H.; ISO 62 | ||
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 119 | 119 | ASTM Test | ||
| Tensile Strength at Break | 62.0 MPa | 8990 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Yield | 64.0 MPa | 9280 psi | 2 in/min; ASTM Test | ||
| 65.0 MPa | 9430 psi | 50mm/min; ISO 527 | |||
| Elongation at Break | 15 % | 15 % | 50mm/min, Nominal strain; ISO 527 | ||
| 15 % | 15 % | 2 in/min; ASTM Test | |||
| 15 % | 15 % | 0.2 in/min; ASTM Test | |||
| Elongation at Yield | 3.0 % | 3.0 % | 50mm/min; ISO 527 | ||
| 3.0 % | 3.0 % | 2 in/min; ASTM Test | |||
| Tensile Modulus | 4.33 GPa | 628 ksi | 1mm/min; ISO 527 | ||
| Flexural Strength | 109 MPa | 15800 psi | ASTM Test | ||
| 30.0 MPa @Temperature 120 °C | 4350 psi @Temperature 248 °F | ASTM Test | |||
| 30.0 MPa @Temperature 93.0 °C | 4350 psi @Temperature 199 °F | ASTM Test | |||
| 45.0 MPa @Temperature 65.0 °C | 6530 psi @Temperature 149 °F | ASTM Test | |||
| 180 MPa @Temperature -40.0 °C | 26100 psi @Temperature -40.0 °F | ASTM Test | |||
| Flexural Modulus | 4.00 GPa | 580 ksi | ASTM Test | ||
| 0.750 GPa @Temperature 120 °C | 109 ksi @Temperature 248 °F | ASTM Test | |||
| 0.770 GPa @Temperature 93.0 °C | 112 ksi @Temperature 199 °F | ASTM Test | |||
| 1.25 GPa @Temperature 65.0 °C | 181 ksi @Temperature 149 °F | ASTM Test | |||
| Izod Impact, Notched | 0.860 J/cm @Thickness 3.17 mm | 1.61 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179 | ||
| 0.300 J/cm² @Temperature -30.0 °C | 1.43 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 23.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 12.8 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ASTM Test | ||
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 275 °C | 527 °F | Injection molding | ||
| Mold Temperature | 95.0 °C | 203 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| UL.UL-C | Yes | ||||