- 密度 [g/cm3]: 1.16
- 吸水率 [%]: 6.5
- 缺口冲击强度: 7.0
- 拉伸强度 [MPa]: 100.0
- 弯曲模量 [MPa]: 2.90
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 | ||
| Water Absorption | 6.5 - 7.5 % | 6.5 - 7.5 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.6 - 2.0 % | 1.6 - 2.0 % | 23°C; 50% RH; ISO 62 | ||
| Viscosity Measurement | 130 | 130 | ISO 307 | ||
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | restricted | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 10.0 MPa @Strain 2.00 %, Temperature 100 °C | 1450 psi @Strain 2.00 %, Temperature 212 °F | 50mm/min | ||
| 20.0 MPa @Strain 5.00 %, Temperature 100 °C | 2900 psi @Strain 5.00 %, Temperature 212 °F | 50mm/min | |||
| 25.0 MPa @Strain 8.00 %, Temperature 100 °C | 3630 psi @Strain 8.00 %, Temperature 212 °F | 50mm/min | |||
| 40.0 MPa @Strain 2.00 %, Temperature 80.0 °C | 5800 psi @Strain 2.00 %, Temperature 176 °F | 50mm/min | |||
| 50.0 MPa @Strain 5.00 %, Temperature 80.0 °C | 7250 psi @Strain 5.00 %, Temperature 176 °F | 50mm/min | |||
| 50.0 MPa @Strain 8.00 %, Temperature 80.0 °C | 7250 psi @Strain 8.00 %, Temperature 176 °F | 50mm/min | |||
| 60.0 MPa @Strain 2.00 %, Temperature 60.0 °C | 8700 psi @Strain 2.00 %, Temperature 140 °F | 50mm/min | |||
| 73.0 MPa @Strain 8.00 %, Temperature 60.0 °C | 10600 psi @Strain 8.00 %, Temperature 140 °F | 50mm/min | |||
| 75.0 MPa @Strain 2.00 %, Temperature 23.0 °C | 10900 psi @Strain 2.00 %, Temperature 73.4 °F | 50mm/min | |||
| 75.0 MPa @Strain 5.00 %, Temperature 60.0 °C | 10900 psi @Strain 5.00 %, Temperature 140 °F | 50mm/min | |||
| 80.0 MPa @Strain 8.00 %, Temperature 23.0 °C | 11600 psi @Strain 8.00 %, Temperature 73.4 °F | 50mm/min | |||
| 110 MPa @Strain 5.00 %, Temperature 23.0 °C | 16000 psi @Strain 5.00 %, Temperature 73.4 °F | 50mm/min | |||
| Tensile Strength, Yield | 100 MPa | 14500 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 8.0 % | 8.0 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 3.20 GPa | 464 ksi | ISO 527-1/-2 | ||
| 1.75 GPa @Temperature 100 °C | 254 ksi @Temperature 212 °F | ISO 527 | |||
| 3.00 GPa @Temperature 80.0 °C | 435 ksi @Temperature 176 °F | ISO 527 | |||
| 3.50 GPa @Temperature 60.0 °C | 508 ksi @Temperature 140 °F | ISO 527 | |||
| 3.75 GPa @Temperature 40.0 °C | 544 ksi @Temperature 104 °F | ISO 527 | |||
| Flexural Modulus | 2.90 GPa | 421 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature 23.0 °C | 3.33 ft-lb/in² @Temperature 73.4 °F | ISO 180/A | ||
| Charpy Impact Unnotched | 10.5 J/cm² @Temperature -30.0 °C | 50.0 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 12.0 J/cm² @Temperature 23.0 °C | 57.1 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 1.30 J/cm² @Temperature 23.0 °C | 6.19 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 4.0 @Frequency 1.00 Hz | 4.0 @Frequency 1.00 Hz | IEC 60250 | ||
| Dissipation Factor | 0.030 @Frequency 1.00e+6 Hz | 0.030 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 0.600 - 0.800 µm/m-°C @Temperature 23.0 - 80.0 °C | 0.333 - 0.444 µin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | |||
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 295 °C | 563 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 110 °C | 230 °F | for 50% loss of tensile strength after 20000hr | ||
| 130 °C | 266 °F | for 50% loss of tensile strength after 5000hr | |||
| 250 °C | 482 °F | ||||
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 310 - 330 °C | 590 - 626 °F | Injection-molding/Extrusion | ||
| Mold Temperature | 70.0 - 100 °C | 158 - 212 °F | Injection-molding | ||
| Descriptive Properties | |||||
| Commercial Status | Europe | ||||