- 密度 [g/cm3]: 1.13
- 缺口冲击强度: 0.53
- 拉伸强度 [MPa]: 24.0
- 弯曲模量 [MPa]: 0.260
- 硬度: 99.0
- 热变形温度 [℃]: 169.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 | ||
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | 24 Hours; ASTM D570 | ||
| 2.6 % | 2.6 % | 50% RH; ASTM D570 | |||
| 9.2 % | 9.2 % | Saturation; ASTM D570 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 99 | 99 | ASTM D785 | ||
| Tensile Strength, Yield | 24.0 MPa @Temperature 121 °C | 3480 psi @Temperature 250 °F | ASTM D638 | ||
| 84.0 MPa @Temperature 23.0 °C | 12200 psi @Temperature 73.4 °F | ASTM D638 | |||
| 138 MPa @Temperature -40.0 °C | 20000 psi @Temperature -40.0 °F | ASTM D638 | |||
| Elongation at Break | >= 100 % | >= 100 % | ASTM D638 | ||
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 | ||
| Flexural Strength | 17.0 MPa @Temperature 121 °C | 2470 psi @Temperature 250 °F | ASTM D790 | ||
| 20.0 MPa @Temperature 90.0 °C | 2900 psi @Temperature 194 °F | ASTM D790 | |||
| 30.0 MPa @Temperature 65.0 °C | 4350 psi @Temperature 149 °F | ASTM D790 | |||
| 114 MPa @Temperature 23.0 °C | 16500 psi @Temperature 73.4 °F | ASTM D790 | |||
| 179 MPa @Temperature -40.0 °C | 26000 psi @Temperature -40.0 °F | ASTM D790 | |||
| Flexural Modulus | 0.260 GPa @Temperature 121 °C | 37.7 ksi @Temperature 250 °F | ASTM D790 | ||
| 0.310 GPa @Temperature 90.0 °C | 45.0 ksi @Temperature 194 °F | ASTM D790 | |||
| 0.435 GPa @Temperature 65.0 °C | 63.1 ksi @Temperature 149 °F | ASTM D790 | |||
| 2.90 GPa @Temperature 23.0 °C | 421 ksi @Temperature 73.4 °F | ASTM D790 | |||
| 3.16 GPa @Temperature -40.0 °C | 458 ksi @Temperature -40.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 0.530 J/cm @Temperature -40.0 °C | 0.993 ft-lb/in @Temperature -40.0 °F | ASTM D256 | ||
| 0.530 J/cm @Temperature 23.0 °C | 0.993 ft-lb/in @Temperature 73.4 °F | ASTM D256 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 1.35 µm/m-°C | 0.750 µin/in-°F | ASTM E831 | ||
| Melting Point | 220 °C | 428 °F | ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 169 °C | 336 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 63.0 °C | 145 °F | ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 245 - 260 °C | 473 - 500 °F | |||
| Mold Temperature | 60.0 °C | 140 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | <= 0.15 % | <= 0.15 % | |||
| Descriptive Properties | |||||
| Color | BK 102 | ||||
| Commercial Status | North America | ||||