- 密度 [g/cm3]: 1.8
- 弯曲模量 [MPa]: 11.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.80 g/cc | 0.0650 lb/in³ | |||
| Filler Content | 47 % | 47 % | by volume | ||
| Thickness | 500 microns | 19.7 mil | laminate layer thickness | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 125 MPa | 18100 psi | transverse; ISO 527-4/5 | ||
| 605 MPa | 87700 psi | longitudinal; ISO 527-4/5 | |||
| Elongation at Break | 1.5 % | 1.5 % | transverse; ISO 527-4/5 | ||
| 2.1 % | 2.1 % | longitudinal; ISO 527-4/5 | |||
| Tensile Modulus | 12.0 GPa | 1740 ksi | transverse; ISO 527-4/5 | ||
| 30.1 GPa | 4370 ksi | longitudinal; ISO 527-4/5 | |||
| Flexural Strength | 175 MPa | 25400 psi | transverse; ISO 178 | ||
| 840 MPa | 122000 psi | longitudinal; ISO 178 | |||
| Flexural Modulus | 11.0 GPa | 1600 ksi | transverse; ISO 178 | ||
| 26.5 GPa | 3840 ksi | longitudinal; ISO 178 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | DSC 3146 | ||
| Maximum Service Temperature, Air | 120 °C @Time 7.20e+7 sec | 248 °F @Time 20000 hour | Relative Temperature Index; IEC 216/1 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75-1/2 | ||
| Minimum Service Temperature, Air | -30.0 °C | -22.0 °F | |||
| Glass Transition Temp, Tg | 60.0 °C | 140 °F | DSC 3146 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 240 - 260 °C | 464 - 500 °F | |||
| Descriptive Properties | |||||
| Reinforcement | Area weight | 600 g/m² | |||
| Fabric | twill | ||||
| Fibers | roving glass | ||||
| Weight Rate | 50% longitudinal, 20% transverse | ||||
| Yarn | 1200 tex longitudinal and transverse | ||||