- 密度 [g/cm3]: 1.27
- 吸水率 [%]: 8.0
- 热变形温度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 | ||
| Water Absorption | 8.0 % | 8.0 % | Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.4 % | 2.4 % | Humidity Absorption; Sim. to ISO 62 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 135 MPa | 19600 psi | ISO 527-1/-2 | ||
| Elongation at Break | 4.0 % | 4.0 % | ISO 527-1/-2 | ||
| Tensile Modulus | 7.20 GPa | 1040 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 8.00 J/cm² @Temperature 23.0 °C | 38.1 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 1.10 J/cm² @Temperature 23.0 °C | 5.24 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 | ||
| Descriptive Properties | |||||
| Blow Molding | Yes | ||||
| Heat Stabilized or Stable to Heat | Yes | ||||
| With Fillers | Yes | ||||