- 熔体流动速率 [g/10min]: 27.6
- 密度 [g/cm3]: 1.38
- 吸水率 [%]: 6.2
- 热变形温度 [℃]: 205.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 | ||
| Water Absorption | 6.2 % | 6.2 % | Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.8 % | 1.8 % | Humidity Absorption; Sim. to ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | Parallel; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | Normal; ISO 294-4 | ||
| Melt Flow | 27.6 g/10 min @Load 2.16 kg, Temperature 250 °C | 27.6 g/10 min @Load 4.76 lb, Temperature 482 °F | Calculated from Volume Flow Rate of 20 cm3/10min.; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527-1/-2 | ||
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 | ||
| Tensile Modulus | 6.20 GPa | 899 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 3.50 J/cm² @Temperature 23.0 °C | 16.7 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.500 J/cm² @Temperature 23.0 °C | 2.38 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| >= 600 V | >= 600 V | PLC 0; UL 746A | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature 20.0 °C | 27.8 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature 20.0 °C | 27.8 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ISO 75-1/-2 | ||
| UL RTI, Electrical | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | UL746B | ||
| 65.0 °C @Thickness 0.750 mm | 149 °F @Thickness 0.0295 in | UL746B | |||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.750 mm | 149 °F @Thickness 0.0295 in | UL746B | ||
| 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | UL746B | |||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | UL746B | ||
| 65.0 °C @Thickness 0.750 mm | 149 °F @Thickness 0.0295 in | UL746B | |||
| Flammability, UL94 | V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | IEC 60695-11-10 | ||
| V-2 @Thickness 0.750 mm | V-2 @Thickness 0.0295 in | IEC 60695-11-10 | |||
| Glow Wire Test | 700 °C @Thickness 0.750 mm | 1290 °F @Thickness 0.0295 in | Glow Wire Ignition Temperature; IEC 60695-2-13 | ||
| 725 °C @Thickness 3.00 mm | 1340 °F @Thickness 0.118 in | Glow Wire Ignition Temperature; IEC 60695-2-13 | |||
| 960 °C @Thickness 0.750 mm | 1760 °F @Thickness 0.0295 in | Glow Wire Flammability Index; IEC 60695-2-12 | |||
| 960 °C @Thickness 3.00 mm | 1760 °F @Thickness 0.118 in | Glow Wire Flammability Index; IEC 60695-2-12 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 | ||
| Descriptive Properties | |||||
| Flame Retardant | Yes | ||||
| Flame Retarding Agent | Yes | ||||
| Heat Stabilized or Stable to Heat | Yes | ||||
| Injection Molding | Yes | ||||
| Release Agent | Yes | ||||
| RSV Formic Acid | 2.25 g/100ml | ISO 307 | |||
| With Fillers | Yes | ||||