- 密度 [g/cm3]: 1.14
- 缺口冲击强度: 62.0
- 弯曲强度 [MPa]: 37.0
- 弯曲模量 [MPa]: 1.045
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 67 | 67 | ISO 868 |
| Tensile Strength, Ultimate | 37.0 MPa | 5370 psi | ISO 527 |
| Elongation at Break | 350 % | 350 % | ISO 527 |
| Modulus of Elasticity | 0.978 GPa | 142 ksi | ISO 527 |
| Flexural Modulus | 1.045 GPa | 151.6 ksi | ISO 178 |
| Shear Modulus | 0.450 GPa | 65.3 ksi | torsional |
| Izod Impact, Notched (ISO) | 62.0 kJ/m² | 29.5 ft-lb/in² | ISO 180, Ductile break |
| 16.0 kJ/m² @Temperature -40.0 °C | 7.61 ft-lb/in² @Temperature -40.0 °F | Ductile break; ISO 180 | |
| Charpy Impact, Notched | 4.20 J/cm² | 20.0 ft-lb/in² | DIN 53453, Ductile break |
| 2.80 J/cm² @Temperature -40.0 °C | 13.3 ft-lb/in² @Temperature -40.0 °F | Ductile break; DIN 53453 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 213 °C | 415 °F | DSC |