- 熔体流动速率 [g/10min]: 50.0
- 密度 [g/cm3]: 1.02
- 拉伸强度 [MPa]: 39.0
- 热变形温度 [℃]: 143.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | |
| Melt Flow | 50 g/10 min @Load 2.16 kg, Temperature 235 °C | 50 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 39.0 MPa | 5660 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 12 % | 12 % | 50 mm/min |
| Tensile Modulus | 1.38 GPa | 200 ksi | 1 mm/min |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Strength | 55.0 kV/mm | 1400 kV/in | |
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature 20.0 °C | 50.0 µin/in-°F @Temperature 68.0 °F | |
| Melting Point | 174 °C | 345 °F | (Dry) |
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 289 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | |
| Vicat Softening Point | 145 °C | 293 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| V-2 @Thickness 3.20 mm | V-2 @Thickness 0.126 in | ||