- 熔体流动速率 [g/10min]: 3.7
- 密度 [g/cm3]: 1.2
- 吸水率 [%]: 1.1
- 弯曲强度 [MPa]: 104.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | |
| Water Absorption | 1.1 % | 1.1 % | |
| Melt Flow | 3.7 g/10 min @Load 2.16 kg, Temperature 235 °C | 3.7 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 104 MPa | 15100 psi | 5 mm/min |
| Elongation at Break | 5.0 % | 5.0 % | 5 mm/min |
| Tensile Modulus | 7.11 GPa | 1030 ksi | 1 mm/min |
| Charpy Impact Unnotched | 7.13 J/cm² | 33.9 ft-lb/in² | |
| 7.91 J/cm² @Temperature -30.0 °C | 37.6 ft-lb/in² @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 1.29 J/cm² | 6.14 ft-lb/in² | |
| 0.950 J/cm² @Temperature -30.0 °C | 4.52 ft-lb/in² @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 17.5 kV/mm | 445 kV/in | |
| Dissipation Factor | 0.000335 @Frequency 1e+6 Hz | 0.000335 @Frequency 1e+6 Hz | |
| 0.000369 @Frequency 100 Hz | 0.000369 @Frequency 100 Hz | ||
| Comparative Tracking Index | 100 V | 100 V | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 174 °C | 345 °F | 10°C/min |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.10 mm | HB @Thickness 0.122 in | ||