- 密度 [g/cm3]: 1.48
- 缺口冲击强度: 0.97
- 拉伸强度 [MPa]: 113.0
- 断裂伸长率 [%]: 148
- 弯曲模量 [MPa]: 8.93
- 热变形温度 [℃]: 176.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ASTM D792 |
| 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec | 0.0020 - 0.0040 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.010 cm/cm @Time 86400 sec | 0.0080 - 0.010 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 113 MPa | 16400 psi | 5 mm/min; ISO 527 |
| 121 MPa | 17500 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 113 MPa | 16400 psi | 5 mm/min; ISO 527 |
| 121 MPa | 17500 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 1.7 % | 1.7 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 1.7 % | 1.7 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 12.28 GPa | 1781 ksi | 1 mm/min; ISO 527 |
| 12.8 GPa | 1860 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 143 MPa | 20700 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 148 MPa | 21500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 8.93 GPa | 1300 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.970 J/cm | 1.82 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.77 J/cm | 10.8 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 1.00 kJ/m² | 0.476 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Impact Test | 16.0 J | 11.8 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 176 °C @Thickness 3.20 mm | 349 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 176 °C | 349 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 166 °C @Thickness 3.20 mm | 331 °F @Thickness 0.126 in | unannealed; ASTM D648 | |