- 熔体流动速率 [g/10min]: 7.9
- 密度 [g/cm3]: 1.08
- 吸水率 [%]: 1.4
- 拉伸强度 [MPa]: 28.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | |
| Water Absorption | 1.4 % | 1.4 % | |
| Melt Flow | 7.9 g/10 min @Load 2.16 kg, Temperature 235 °C | 7.9 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 38 % | 38 % | 50 mm/min |
| Tensile Modulus | 0.605 GPa | 87.7 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | Low Temp |
| NB | NB | ||
| Charpy Impact, Notched | 3.80 J/cm² | 18.1 ft-lb/in² | Partial Break |
| 0.430 J/cm² @Temperature -30.0 °C | 2.05 ft-lb/in² @Temperature -22.0 °F | ||
| Thermal Properties | Metric | English | Comments |
| Melting Point | 178 °C | 352 °F | 10°C/min |
| Flammability, UL94 | V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | |
| V-2 @Thickness 3.20 mm | V-2 @Thickness 0.126 in | ||
| Oxygen Index | 27 % | 27 % | |