- 密度 [g/cm3]: 1.07
- 吸水率 [%]: 1.3
- 成型收缩率 [%]: 0.011
- 缺口冲击强度: 0.37
- 拉伸强度 [MPa]: 59.0
- 弯曲模量 [MPa]: 2.14
- 硬度: 114.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | DAM; ASTM D792 | ||
| Density | 1.07 g/cc | 0.0387 lb/in³ | DAM; ISO 1183 | ||
| Water Absorption | 1.3 % @Temperature 23.0 °C | 1.3 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | ||
| 3.0 % @Temperature 23.0 °C | 3.0 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
| Linear Mold Shrinkage | 0.011 cm/cm @Thickness 3.20 mm | 0.011 in/in @Thickness 0.126 in | Flow; DAM | ||
| 0.011 cm/cm @Thickness 3.20 mm | 0.011 in/in @Thickness 0.126 in | Transverse; DAM | |||
| Linear Mold Shrinkage, Flow | 0.013 cm/cm @Thickness 2.00 mm | 0.013 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm @Thickness 2.00 mm | 0.014 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 114 | 114 | DAM; ISO 2039/2 | ||
| Tensile Strength | 62.0 MPa @Temperature 23.0 °C | 8990 psi @Temperature 73.4 °F | DAM; ASTM D638 | ||
| Tensile Strength, Yield | 59.0 MPa @Temperature 23.0 °C | 8560 psi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Elongation at Break | 38 % @Temperature 23.0 °C | 38 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | ||
| 50 % @Temperature 23.0 °C | 50 % @Temperature 73.4 °F | DAM; ASTM D638 | |||
| Elongation at Yield | 13 % @Temperature 23.0 °C | 13 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| Tensile Modulus | 2.40 GPa @Temperature 23.0 °C | 348 ksi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Flexural Modulus | 2.14 GPa @Temperature 23.0 °C | 310 ksi @Temperature 73.4 °F | DAM; ASTM D790 | ||
| 2.20 GPa @Temperature 23.0 °C | 319 ksi @Temperature 73.4 °F | DAM; ISO 178 | |||
| Izod Impact, Notched | 0.370 J/cm @Temperature 23.0 °C | 0.693 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D256 | ||
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | DAM; ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.480 J/cm² @Temperature 23.0 °C | 2.28 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 218 °C | 424 °F | DAM; ASTM D3418 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 63.0 °C | 145 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 218 °C | 424 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 250 °C | 482 °F | DAM; Optimum | |||
| 230 - 290 °C | 446 - 554 °F | DAM | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; optimum | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.15 % | <= 0.15 % | DAM | ||
| Descriptive Properties | |||||
| Appearance | Natural Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 612 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA612< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA612 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Unreinforced Resins | DAM | |||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA612 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||