- 密度 [g/cm3]: 1.28
- 吸水率 [%]: 0.8
- 弯曲强度 [MPa]: 137.0
- 热变形温度 [℃]: 213.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ISO 1183 |
| Water Absorption | 0.80 % | 0.80 % | ISO 62 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | normal; ISO 294-4,2577 |
| Linear Mold Shrinkage, Flow | 0.010 cm/cm | 0.010 in/in | parallel; ISO 294-4,2577 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 137 MPa | 19900 psi | ISO527-2/1A |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527-2/1A |
| Tensile Modulus | 7.80 GPa | 1130 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 9.00 J/cm² @Temperature 23.0 °C | 42.8 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU |
| 9.00 J/cm² @Temperature -30.0 °C | 42.8 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 1.30 J/cm² @Temperature -30.0 °C | 6.19 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA |
| 2.00 J/cm² @Temperature 23.0 °C | 9.52 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ISO 60695 |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 215 °C | 419 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | ISO 75-1/2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | ISO 75-1/2 |
| Vicat Softening Point | 210 °C | 410 °F | ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC60695 |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | IEC60695 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 250 - 290 °C | 482 - 554 °F | |
| Mold Temperature | 60.0 - 110 °C | 140 - 230 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 70.0 - 130 MPa | 10200 - 18900 psi | |