- 密度 [g/cm3]: 1.05
- 吸水率 [%]: 1.5
- 拉伸强度 [MPa]: 45.0
- 热变形温度 [℃]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 | ||
| Water Absorption | 1.5 % | 1.5 % | ISO 62 | ||
| Moisture Absorption | 4.10 % | 4.10 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.016 cm/cm | 0.016 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 50.0 MPa | 7250 psi | conditioned; ISO 2039-1 | ||
| 105 MPa | 15200 psi | dry; ISO 2039-1 | |||
| Tensile Strength at Break | 35.0 MPa | 5080 psi | conditioned; ISO 527-1/-2 | ||
| 40.0 MPa | 5800 psi | dry; ISO 527-1/-2 | |||
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | dry; ISO 527-1/-2 | ||
| 45.0 MPa | 6530 psi | dry; ISO 527-1/-2 | |||
| Elongation at Break | >= 50 % | >= 50 % | dry; ISO 527-1/-2 | ||
| >= 50 % | >= 50 % | conditioned; ISO 527-1/-2 | |||
| Elongation at Yield | 5.0 % | 5.0 % | dry; ISO 527-1/-2 | ||
| 5.0 % | 5.0 % | dry; ISO 527-1/-2 | |||
| Tensile Modulus | 0.700 GPa | 102 ksi | conditioned; ISO 527-1/-2 | ||
| 1.70 GPa | 247 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | NB | NB | dry; ISO 179/1eU | ||
| NB | NB | conditioned; ISO 179/1eU | |||
| NB @Temperature 30.0 °C | NB @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| NB @Temperature 30.0 °C | NB @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Charpy Impact, Notched | NB | NB | dry; ISO 179/1eA | ||
| NB | NB | conditioned; ISO 179/1eA | |||
| 2.00 J/cm² @Temperature 30.0 °C | 9.52 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| 2.10 J/cm² @Temperature 30.0 °C | 9.99 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | conditioned; IEC 60093 | ||
| 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | dry; IEC 60093 | |||
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 | ||
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | conditioned; IEC 60243-1 | ||
| 33.0 kV/mm | 838 kV/in | dry; IEC 60243-1 | |||
| Comparative Tracking Index | 600 V | 600 V | conditioned; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 150 µm/m-°C | 83.3 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 150 µm/m-°C | 83.3 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB | HB | IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Automotive | Air intake sytems | ||||
| Compressed air systems | |||||
| Hydraulic systems | |||||
| Form | Granules | ||||
| Industry & Consumer goods | Hydraulics & Pneumatics | ||||
| Processing | Other Extrusion | ||||
| Product Attributes | Bio based Polyamide | ||||
| Special Characteristics | Improved heat resistance | ||||