| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ISO 2782 | ||
| Viscosity Measurement | 14 @Temperature 150 °C | 14 @Temperature 302 °F | Kg/cm2; Macklow-Smith extrusion rheometer | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 90 | 90 | ISO 868 | ||
| Tensile Strength | 19.5 MPa | 2830 psi | ISO 37 | ||
| Elongation at Break | 740 % | 740 % | ISO 37 | ||
| 100% Modulus | 0.00430 GPa | 0.624 ksi | ISO 37 | ||
| 200% Modulus | 0.00500 GPa | 0.725 ksi | ISO 37 | ||
| 300% Modulus | 0.00560 GPa | 0.812 ksi | ISO 37 | ||
| Tear Strength | 70.0 kN/m | 399 pli | ISO 34-B | ||
| Abrasion | 62 | 62 | mm3; DIN 53516 | ||
| Compression Set | 31 % @Temperature 22.0 °C, Time 259000 sec | 31 % @Temperature 71.6 °F, Time 72.0 hour | ISO 815 | ||
| 47 % @Temperature 70.0 °C, Time 79200 sec | 47 % @Temperature 158 °F, Time 22.0 hour | ISO 815 | |||
| 60 % @Temperature 100 °C, Time 79200 sec | 60 % @Temperature 212 °F, Time 22.0 hour | ISO 815 | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 125 °C | 257 °F | |||
| Minimum Service Temperature, Air | -60.0 °C | -76.0 °F | |||
| Descriptive Properties | |||||
| Bonds with | Polypropylene | ||||
| Chemical Resistance | Acetone | Moderate/Good | |||
| Acids up to 80% | Excellent | ||||
| Alcohol | Excellent | ||||
| Alkalis | Excellent | ||||
| Brake fluid | Good | ||||
| Chlorinate solvents | Poor | ||||
| Diesel | Poor | ||||
| Ethylene glycol | Excellent | ||||
| Gasoline | Good | ||||
| Salt solution | Excellent | ||||
| Soda lye | Excellent | ||||
| Water, 23°C | Excellent | ||||
| Water, 95°C | Good | ||||