- 密度 [g/cm3]: 1.49
- 吸水率 [%]: 0.11
- 缺口冲击强度: 0.961
- 拉伸强度 [MPa]: 157.0
- 弯曲模量 [MPa]: 10.309
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ASTM D792 |
| Water Absorption | 0.11 % | 0.11 % | at 24 hours; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 103 | 103 | ASTM D785 |
| Tensile Strength, Yield | 157 MPa | 22800 psi | ASTM D638 |
| Elongation at Break | 2.2 % | 2.2 % | ASTM D638 |
| Tensile Modulus | 9.6995 GPa | 1406.8 ksi | 1 % Sec; ASTM D638 |
| Flexural Strength | 233 MPa | 33800 psi | ASTM D790 |
| Flexural Modulus | 10.309 GPa | 1495.2 ksi | Tangent; ASTM D790 |
| Compressive Strength | 215 MPa | 31200 psi | ASTM D695 |
| Shear Strength | 97.2 MPa | 14100 psi | Ultimate; ASTM D3846 |
| Izod Impact, Notched | 0.961 J/cm | 1.80 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Dielectric Strength | 6.89 kV/mm | 175 kV/in | ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 21.6 µm/m-°C @Temperature 20.0 °C | 12.0 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Thermal Conductivity | 0.432 W/m-K | 3.00 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 334 °C | 633 °F | |
| Maximum Service Temperature, Air | 250 °C | 482 °F | Continuous |
| Deflection Temperature at 1.8 MPa (264 psi) | 316 °C | 600 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |