- 密度 [g/cm3]: 1.39
- 缺口冲击强度: 0.48
- 拉伸强度 [MPa]: 62.0
- 弯曲模量 [MPa]: 2.75
- 热变形温度 [℃]: 156.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.39 g/cc | 1.39 g/cc | ASTM D 792 |
| Density | 1.39 g/cc | 0.0502 lb/in³ | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.080 % | 0.080 % | 23°C / 50% RH; ISO 62 |
| 0.070 % @Time 86400 sec | 0.070 % @Time 24.0 hour | 50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0090 - 0.020 cm/cm @Time 86400 sec | 0.0090 - 0.020 in/in @Time 24.0 hour | ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec | 0.010 - 0.030 in/in @Time 24.0 hour | ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 62.0 MPa | 8990 psi | 5 mm/min; ISO 527 |
| 64.0 MPa | 9280 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | 5 mm/min; ISO 527 |
| 64.0 MPa | 9280 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 3.3 % | 3.3 % | 5 mm/min; ISO 527 |
| 4.5 % | 4.5 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 3.3 % | 3.3 % | 5 mm/min; ISO 527 |
| 4.5 % | 4.5 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 3.00 GPa | 435 ksi | 50 mm/min; ASTM D 638 |
| 3.07 GPa | 445 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 92.0 MPa | 13300 psi | ISO 178 |
| Flexural Modulus | 2.75 GPa | 399 ksi | 2 mm/min; ISO 178 |
| 2.94 GPa | 426 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.480 J/cm @Temperature 23.0 °C | 0.899 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Unnotched | 7.23 J/cm @Temperature 23.0 °C | 13.5 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C | 2.38 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 37.0 kJ/m² @Temperature 23.0 °C | 17.6 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1U |
| Impact Test | 3.00 J @Temperature 23.0 °C | 2.21 ft-lb @Temperature 73.4 °F | Instrumented Impact Total Energy; ASTM D 3763 |
| Coefficient of Friction, Dynamic | 0.42 | 0.42 | ASTM D 3702 Modified |
| Coefficient of Friction, Static | 0.32 | 0.32 | ASTM D 3702 Modified |
| K (wear) Factor | 36.3 x 10-8 mm³/N-M | 18.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D 3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 47.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 26.1 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D 696 |
| CTE, linear, Transverse to Flow | 57.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 31.7 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C | 313 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 156 °C @Thickness 3.20 mm | 313 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 147 °C | 297 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 146 °C @Thickness 3.20 mm | 295 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |