- 密度 [g/cm3]: 1.4
- 缺口冲击强度: 0.75
- 拉伸强度 [MPa]: 78.0
- 弯曲模量 [MPa]: 3.20
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | Crystalline; ISO 1183 |
| Viscosity | 340000 cP @Temperature 400 °C | 340000 cP @Temperature 752 °F | melt; ISO 11443 |
| Linear Mold Shrinkage, Flow | 0.012 cm/cm | 0.012 in/in | 360°C nozzle, 160°C tool; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.017 cm/cm | 0.017 in/in | 375°C nozzle, 180°C tool; ISO 294-4 |
| Spiral Flow | 130 cm @Thickness 1.00 mm | 51.2 in @Thickness 0.0394 in | 375°C nozzle, 180°C tool |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 78.0 MPa @Temperature 23.0 °C | 11300 psi @Temperature 73.4 °F | ISO 527 |
| Elongation at Break | 25 % @Temperature 23.0 °C | 25 % @Temperature 73.4 °F | ISO 527 |
| Tensile Modulus | 2.90 GPa @Temperature 23.0 °C | 421 ksi @Temperature 73.4 °F | ISO 527 |
| Flexural Strength | 125 MPa @Temperature 23.0 °C | 18100 psi @Temperature 73.4 °F | ISO 178 |
| Flexural Modulus | 3.20 GPa @Temperature 23.0 °C | 464 ksi @Temperature 73.4 °F | ISO 178 |
| Compressive Strength | 65.0 MPa @Temperature 120 °C | 9430 psi @Temperature 248 °F | ISO 604 |
| 105 MPa @Temperature 23.0 °C | 15200 psi @Temperature 73.4 °F | ISO 604 | |
| Izod Impact, Notched (ISO) | 0.750 kJ/m² @Temperature 23.0 °C | 0.357 ft-lb/in² @Temperature 73.4 °F | ISO 180/A |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 2.8 @Frequency 1000 Hz, Temperature 23.0 °C | 2.8 @Frequency 1000 Hz, Temperature 73.4 °F | IEC 60250 |
| Dielectric Strength | 21.0 kV/mm @Thickness 2.50 mm | 533 kV/in @Thickness 0.0984 in | IEC 60243-1 |
| Dissipation Factor | 0.0040 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.0040 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | IEC 60250 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 40.0 µm/m-°C @Temperature <=143 °C | 22.2 µin/in-°F @Temperature <=289 °F | Along flow below Tg; ISO 11359 |
| 60.0 µm/m-°C @Temperature <=143 °C | 33.3 µin/in-°F @Temperature <=289 °F | Average below Tg; ISO 11359 | |
| 120 µm/m-°C @Temperature >=143 °C | 66.7 µin/in-°F @Temperature >=289 °F | Along flow above Tg; ISO 11359 | |
| 140 µm/m-°C @Temperature >=143 °C | 77.8 µin/in-°F @Temperature >=289 °F | Average above Tg; ISO 11359 | |
| Melting Point | 343 °C | 649 °F | ISO 11357 |
| Glass Transition Temp, Tg | 143 °C | 289 °F | Onset; ISO 11357 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
| Drying Temperature | 120 °C @Time 18000 sec | 248 °F @Time 5.00 hour | |
| 150 °C @Time 10800 sec | 302 °F @Time 3.00 hour | ||