- 密度 [g/cm3]: 1.44
- 吸水率 [%]: 0.03
- 缺口冲击强度: 0.85
- 弯曲模量 [MPa]: 28.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | Crystalline; ISO 1183 | ||
| Water Absorption | 0.030 % @Temperature 23.0 °C, Time 86400 sec | 0.030 % @Temperature 73.4 °F, Time 24.0 hour | 3.2mm thick tensile bar; ISO 62-1 | ||
| Water Absorption at Saturation | 0.30 % @Temperature 23.0 °C | 0.30 % @Temperature 73.4 °F | Equilibrium; by immersion; ISO 62-1 | ||
| Viscosity | 850000 cP @Temperature 400 °C | 850000 cP @Temperature 752 °F | melt; ISO 11443 | ||
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | 360°C nozzle, 160°C tool; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | 405°C nozzle, 200°C tool; ISO 294-4 | ||
| Spiral Flow | 65.0 cm @Thickness 1.00 mm | 25.6 in @Thickness 0.0394 in | 405°C nozzle, 200°C tool | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 250 MPa @Temperature 23.0 °C | 36300 psi @Temperature 73.4 °F | ISO 527 | ||
| Elongation at Break | 1.5 % @Temperature 23.0 °C | 1.5 % @Temperature 73.4 °F | ISO 527 | ||
| Tensile Modulus | 32.0 GPa @Temperature 23.0 °C | 4640 ksi @Temperature 73.4 °F | ISO 527 | ||
| Flexural Strength | 380 MPa @Temperature 23.0 °C | 55100 psi @Temperature 73.4 °F | ISO 178 | ||
| Flexural Modulus | 28.0 GPa @Temperature 23.0 °C | 4060 ksi @Temperature 73.4 °F | ISO 178 | ||
| Izod Impact, Notched (ISO) | 0.850 kJ/m² @Temperature 23.0 °C | 0.404 ft-lb/in² @Temperature 73.4 °F | ISO 180/A | ||
| Izod Impact, Unnotched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C | 1.90 ft-lb/in² @Temperature 73.4 °F | ISO 180/U | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 5.00 µm/m-°C @Temperature <=143 °C | 2.78 µin/in-°F @Temperature <=289 °F | Along flow below Tg; ISO 11359 | ||
| 8.00 µm/m-°C @Temperature >=143 °C | 4.44 µin/in-°F @Temperature >=289 °F | Along flow above Tg; ISO 11359 | |||
| 35.0 µm/m-°C @Temperature <=143 °C | 19.4 µin/in-°F @Temperature <=289 °F | Average below Tg; ISO 11359 | |||
| 90.0 µm/m-°C @Temperature >=143 °C | 50.0 µin/in-°F @Temperature >=289 °F | Average above Tg; ISO 11359 | |||
| Specific Heat Capacity | 1.80 J/g-°C @Temperature 23.0 °C | 0.430 BTU/lb-°F @Temperature 73.4 °F | DSC | ||
| Melting Point | 343 °C | 649 °F | ISO 11357 | ||
| Glass Transition Temp, Tg | 143 °C | 289 °F | Onset; ISO 11357 | ||
| Flammability, UL94 | V-0 @Thickness 0.500 mm | V-0 @Thickness 0.0197 in | |||
| Glow Wire Test | 960 °C @Thickness 2.00 mm | 1760 °F @Thickness 0.0787 in | IEC 60695-2-12 | ||
| Processing Properties | Metric | English | Comments | ||
| Mold Temperature | 190 - 210 °C | 374 - 410 °F | |||
| Drying Temperature | 120 °C @Time 18000 sec | 248 °F @Time 5.00 hour | |||
| 150 °C @Time 10800 sec | 302 °F @Time 3.00 hour | ||||
| Descriptive Properties | |||||
| Toxicity Index | 0.05 | NES 713; CO content | |||
| 0.12 | NES 713; CO2 content | ||||
| 0.17 | NES 713; Total gases | ||||