Victrex® PEEK 90CA30 Polyetheretherketone, 30% Carbon Fibre Reinforced

Victrex® PEEK 90CA30 Polyetheretherketone, 30% Carbon Fibre Reinforced 物性表: Victrex® PEEK 90CA30 Polyetheretherketone, 30% Carbon Fibre Reinforced物性表及特性介绍,Victrex® PEEK 90CA30 Polyetheretherketone, 30% Carbon Fibre Reinforced注塑参数详情,如需Victrex® PEEK 90CA30 Polyetheretherketone, 30% Carbon Fibre Reinforced下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.4
  • 吸水率 [%]: 0.04
  • 缺口冲击强度: 0.6
  • 弯曲模量 [MPa]: 24.0
 
Physical PropertiesMetricEnglishComments
Density 1.40 g/cc0.0506 lb/in³Crystalline; ISO 1183
Water Absorption 0.040 %
@Temperature 23.0 °C,
Time 86400 sec
0.040 %
@Temperature 73.4 °F,
Time 24.0 hour
3.2mm thick tensile bar; ISO 62-1
Water Absorption at Saturation 0.30 %
@Temperature 23.0 °C
0.30 %
@Temperature 73.4 °F
Equilibrium; by immersion; ISO 62-1
Viscosity 260000 cP
@Temperature 400 °C
260000 cP
@Temperature 752 °F
melt; ISO 11443
Linear Mold Shrinkage, Flow 0.0010 cm/cm0.0010 in/in360°C nozzle, 160°C tool; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0050 cm/cm0.0050 in/in380°C nozzle, 190°C tool; ISO 294-4
Spiral Flow 130 cm
@Thickness 1.00 mm
51.2 in
@Thickness 0.0394 in
380°C nozzle, 190°C tool
 
Mechanical PropertiesMetricEnglishComments
Hardness, Shore D 91
@Temperature 23.0 °C
91
@Temperature 73.4 °F
ISO 868
Tensile Strength at Break  65.0 MPa
@Temperature 275 °C
9430 psi
@Temperature 527 °F
ISO 527
 85.0 MPa
@Temperature 225 °C
12300 psi
@Temperature 437 °F
ISO 527
 110 MPa
@Temperature 175 °C
16000 psi
@Temperature 347 °F
ISO 527
 180 MPa
@Temperature 125 °C
26100 psi
@Temperature 257 °F
ISO 527
 260 MPa
@Temperature 23.0 °C
37700 psi
@Temperature 73.4 °F
ISO 527
Elongation at Break 1.3 %
@Temperature 23.0 °C
1.3 %
@Temperature 73.4 °F
ISO 527
Tensile Modulus 27.0 GPa
@Temperature 23.0 °C
3920 ksi
@Temperature 73.4 °F
ISO 527
Flexural Strength  60.0 MPa
@Temperature 225 °C
8700 psi
@Temperature 437 °F
ISO 178
 120 MPa
@Temperature 175 °C
17400 psi
@Temperature 347 °F
ISO 178
 250 MPa
@Temperature 125 °C
36300 psi
@Temperature 257 °F
ISO 178
 360 MPa
@Temperature 23.0 °C
52200 psi
@Temperature 73.4 °F
ISO 178
Flexural Modulus 24.0 GPa
@Temperature 23.0 °C
3480 ksi
@Temperature 73.4 °F
ISO 178
Compressive Strength  70.0 MPa
@Temperature 200 °C
10200 psi
@Temperature 392 °F
ISO 604
 200 MPa
@Temperature 120 °C
29000 psi
@Temperature 248 °F
ISO 604
 300 MPa
@Temperature 23.0 °C
43500 psi
@Temperature 73.4 °F
ISO 604
Izod Impact, Notched (ISO) 0.600 kJ/m²
@Temperature 23.0 °C
0.286 ft-lb/in²
@Temperature 73.4 °F
ISO 180/A
Izod Impact, Unnotched (ISO) 3.50 kJ/m²
@Temperature 23.0 °C
1.67 ft-lb/in²
@Temperature 73.4 °F
ISO 180/U
 
Thermal PropertiesMetricEnglishComments
CTE, linear  5.00 µm/m-°C
@Temperature <=143 °C
2.78 µin/in-°F
@Temperature <=289 °F
Along flow below Tg; ISO 11359
 5.00 µm/m-°C
@Temperature >=143 °C
2.78 µin/in-°F
@Temperature >=289 °F
Along flow above Tg; ISO 11359
 40.0 µm/m-°C
@Temperature <=143 °C
22.2 µin/in-°F
@Temperature <=289 °F
Average below Tg; ISO 11359
 90.0 µm/m-°C
@Temperature >=143 °C
50.0 µin/in-°F
@Temperature >=289 °F
Average above Tg; ISO 11359
Specific Heat Capacity 1.80 J/g-°C
@Temperature 23.0 °C
0.430 BTU/lb-°F
@Temperature 73.4 °F
DSC
Thermal Conductivity 0.960 W/m-K
@Temperature 23.0 °C
6.66 BTU-in/hr-ft²-°F
@Temperature 73.4 °F
ISO/CD 22007-4
Melting Point 343 °C649 °FISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 342 °C648 °FISO 75A-f
Glass Transition Temp, Tg 143 °C289 °FOnset; ISO 11357
Flammability, UL94 V-0
@Thickness 0.500 mm
V-0
@Thickness 0.0197 in
Glow Wire Test 960 °C
@Thickness 2.00 mm
1760 °F
@Thickness 0.0787 in
IEC 60695-2-12
 
Processing PropertiesMetricEnglishComments
Mold Temperature 170 - 200 °C338 - 392 °F
Drying Temperature  120 °C
@Time 18000 sec
248 °F
@Time 5.00 hour
 150 °C
@Time 10800 sec
302 °F
@Time 3.00 hour
 
Descriptive Properties
Toxicity Index0.05NES 713; CO content
 0.12NES 713; CO2 content
 0.17NES 713; Total gases

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-50384.html

免责声明: 本文 Victrex® PEEK 90CA30 Polyetheretherketone, 30% Carbon Fibre Reinforced 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4