- 密度 [g/cm3]: 1.48
- 吸水率 [%]: 0.05
- 拉伸强度 [MPa]: 64.0
- 弯曲模量 [MPa]: 7.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.050 % @Temperature 23.0 °C | 0.050 % @Temperature 73.4 °F | RMC 93%; DIN EN ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | DIN EN ISO 62 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | >= 100 | >= 100 | DIN 53505 | ||
| Hardness, Shore D | 88 | 88 | DIN 53505 | ||
| Ball Indentation Hardness | 231 MPa | 33500 psi | DIN 2039 | ||
| Tensile Strength at Break | 2.70 MPa | 392 psi | DIN EN ISO 527 | ||
| Tensile Strength | 142 MPa | 20600 psi | DIN EN ISO 527 | ||
| Tensile Stress | 44.0 MPa @Strain 1.00 %, Time 3.60e+6 sec | 6380 psi @Strain 1.00 %, Time 1000 hour | DIN 53444 | ||
| Tensile Strength, Yield | 64.0 MPa | 9280 psi | Elastic Limit | ||
| 120 MPa | 17400 psi | DIN EN ISO 527 | |||
| Elongation at Break | 4.5 % | 4.5 % | |||
| 4.5 % | 4.5 % | DIN EN ISO 527 | |||
| Elongation at Yield | 3.9 % | 3.9 % | Elongation at Maximum Force; DIN EN ISO 527 | ||
| Tensile Modulus | 7.80 GPa | 1130 ksi | DIN EN ISO 527 | ||
| Flexural Strength | 150 MPa | 21800 psi | Outer Fiber Stress at 3.5% Outer Fiber Strain; DIN EN ISO 178 | ||
| 210 MPa | 30500 psi | DIN EN ISO 178 | |||
| Flexural Modulus | 7.00 GPa | 1020 ksi | DIN EN ISO 178 | ||
| Compressive Strength | 123 MPa | 17800 psi | Elastic Limit | ||
| 60.0 MPa @Time 3.60e+7 sec | 8700 psi @Time 10000 hour | ||||
| 109 MPa @Time 360000 sec | 15800 psi @Time 100 hour | ||||
| 131 MPa @Time 36.0 sec | 19000 psi @Time 0.0100 hour | ||||
| 95.0 MPa @Strain 3.50 % | 13800 psi @Strain 3.50 % | DIN EN ISO 604 | |||
| Compressive Modulus | 5.454 GPa | 791.0 ksi | DIN EN ISO 604 | ||
| Fatigue Strength | 105 MPa @Frequency 1.00 Hz, Temperature 20.0 °C | 15200 psi @Frequency 1.00 Hz, Temperature 68.0 °F | 10° stress cycles | ||
| K Factor (ISO) | 0.40 µm/km @Temperature 20.0 °C | 0.40 µm/km @Temperature 68.0 °F | |||
| 1.8 µm/km @Temperature 100 °C | 1.8 µm/km @Temperature 212 °F | ||||
| 3.6 µm/km @Temperature 200 °C | 3.6 µm/km @Temperature 392 °F | ||||
| 5.2 µm/km @Temperature 240 °C | 5.2 µm/km @Temperature 464 °F | ||||
| Charpy Impact Unnotched | 2.30 J/cm² | 10.9 ft-lb/in² | EN ISO 179/1eU | ||
| Charpy Impact, Notched | 0.930 J/cm² | 4.43 ft-lb/in² | EN ISO 179/1eA | ||
| Coefficient of Friction, Dynamic | 0.080 @Temperature 100 °C | 0.080 @Temperature 212 °F | Dry Operation | ||
| 0.10 @Temperature 20.0 °C | 0.10 @Temperature 68.0 °F | Dry Operation | |||
| Coefficient of Friction, Static | 0.12 @Temperature 20.0 °C | 0.12 @Temperature 68.0 °F | Dry Operation | ||
| Tensile Creep Modulus, 1000 hours | 4560 MPa | 661000 psi | At 1% Deformation; DIN 53444 | ||
| Limiting Pressure Velocity | 0.250 MPa-m/sec | 7140 psi-ft/min | v = 1m/min | ||
| 0.350 MPa-m/sec | 9990 psi-ft/min | v = 100m/min | |||
| 0.46667 MPa-m/sec | 13323 psi-ft/min | v = 200m/min | |||
| 0.635 MPa-m/sec | 18100 psi-ft/min | v = 10m/min | |||
| Compression Set | 4.8 % | 4.8 % | Elastic Compression Limit | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 30000 ohm-cm | 30000 ohm-cm | IEC 93 | ||
| Surface Resistance | 19000 ohm | 19000 ohm | IEC 93 | ||
| Dielectric Constant | 3.3 @Frequency 110 Hz | 3.3 @Frequency 110 Hz | IEC 250 | ||
| Dielectric Strength | 0.100 kV/mm | 2.54 kV/in | IEC 243 | ||
| Dissipation Factor | 0.0040 | 0.0040 | IEC 112 | ||
| 0.061 @Frequency 1.00 Hz | 0.061 @Frequency 1.00 Hz | ||||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 35.0 µm/m-°C @Temperature <=100 °C | 19.4 µin/in-°F @Temperature <=212 °F | ISO E 830 | ||
| 38.0 µm/m-°C @Temperature <=150 °C | 21.1 µin/in-°F @Temperature <=302 °F | ISO E 831 | |||
| Specific Heat Capacity | 1.06 J/g-°C | 0.253 BTU/lb-°F | DSC | ||
| Thermal Conductivity | 0.240 W/m-K | 1.67 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 340 °C | 644 °F | DSC | ||
| Maximum Service Temperature, Air | 140 °C | 284 °F | Pressed Bushings | ||
| 250 °C | 482 °F | Continuous | |||
| 260 °C | 500 °F | Short Term (3h) | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 270 °C | 518 °F | DIN EN ISO 75 | ||
| Glass Transition Temp, Tg | 146 °C | 295 °F | DSC | ||
| Flammability, UL94 | V-0 | V-0 | |||
| Oxygen Index | 43 % | 43 % | DIN EN ISO 4589 | ||
| Descriptive Properties | |||||
| Alignment Adjustment | 1 | Nominal Scale: 1, low; 10, high | |||
| Chemical Sterilization | 10 | Nominal Scale: 1, low; 10, high | |||
| Color | Anthracite | ||||
| Creep Resistance | 7 | Nominal Scale: 1, low; 10, high | |||
| Dimensional Stability with Thermal Expansion | 7 | Nominal Scale: 1, low; 10, high | |||
| Free from Silicon | Applicable | ||||
| Gamma-rays Radiation Sterilization | 7 | Nominal Scale: 1, low; 10, high | |||
| Injection Molded Parts | Applicable | ||||
| Machined Parts | Applicable | ||||
| Moist Heat Sterilization | 7 | Nominal Scale: 1, low; 10, high | |||
| Plastic Granules | Applicable | ||||
| Resistance Against dust, Dirt, Abrasive Substances | 10 | Nominal Scale: 1, low; 10, high | |||
| Resistance Against Hot Water | 200 | ||||
| Resistance to Chemicals | 8 | Nominal Scale: 1, low; 10, high | |||
| Resistant Against Disinfectant | Applicable | ||||
| Rods up to Øe (de) | Applicable | ||||
| ROHS/WEEE | Applicable | ||||
| Sheets up to Maximum Thickness | Applicable | ||||
| Sliding Velocity | 100 | ||||
| Suitable for Outdoor Use | 6 | Nominal Scale: 1, low; 10, high | |||
| Suitable for Use in Water | Applicable | ||||
| Suitable for Vacuum | Applicable | ||||
| Tubes (hollow rods) up to Øe (de) | Applicable | ||||
| UV Rays Resistance | 9 | Nominal Scale: 1, low; 10, high | |||
| UV-Sterilization | 10 | Nominal Scale: 1, low; 10, high | |||