- 密度 [g/cm3]: 1.48
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 141 MPa | 20500 psi | ISO 527; DIN 53455 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527; DIN 53455 |
| Tensile Modulus | 9.00 GPa | 1310 ksi | ISO 527; DIN 53452 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 22.0 µm/m-°C @Temperature 20.0 °C | 12.2 µin/in-°F @Temperature 68.0 °F | DIN 53752 |
| Thermal Conductivity | 0.240 W/m-K | 1.67 BTU-in/hr-ft²-°F | DIN 53612 Method A |
| Melting Point | 340 °C | 644 °F | ISO 1218 Method A; DIN 53736 |
| Maximum Service Temperature, Air | 260 °C | 500 °F | 5000 hours; 50% Tensile Strength; IEC 216; DIN 53446 |
| 300 °C | 572 °F | a few hours operation | |
| Deflection Temperature at 1.8 MPa (264 psi) | 293 °C | 559 °F | ISO 75; DIN 53461 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | |