- 密度 [g/cm3]: 1.33
- 吸水率 [%]: 0.1
- 拉伸强度 [MPa]: 76.0
- 弯曲模量 [MPa]: 3.90
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.10 % @Temperature 23.0 °C | 0.10 % @Temperature 73.4 °F | RMC 93%; DIN EN ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.50 % | 0.50 % | DIN EN ISO 62 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 100 | 100 | DIN 53505 | ||
| Hardness, Shore D | 87 | 87 | DIN 53505 | ||
| Ball Indentation Hardness | 175 MPa | 25400 psi | DIN 2039 | ||
| Tensile Strength at Break | 90.0 MPa | 13100 psi | DIN EN ISO 527 | ||
| Tensile Strength | 92.0 MPa | 13300 psi | DIN EN ISO 527 | ||
| Tensile Stress | 26.0 MPa @Strain 1.00 %, Time 3.60e+6 sec | 3770 psi @Strain 1.00 %, Time 1000 hour | DIN 53444 | ||
| Tensile Strength, Yield | 76.0 MPa | 11000 psi | Elastic Limit | ||
| 92.0 MPa | 13300 psi | DIN EN ISO 527 | |||
| Elongation at Break | 23.9 % | 23.9 % | |||
| 23.9 % | 23.9 % | DIN EN ISO 527 | |||
| Elongation at Yield | 1.5 % | 1.5 % | Elastic Yield Point | ||
| 5.7 % | 5.7 % | Flexural; DIN EN ISO 178 | |||
| 6.9 % | 6.9 % | Elongation at Maximum Force; DIN EN ISO 527 | |||
| 6.9 % | 6.9 % | Yield Strain; DIN EN ISO 527 | |||
| Tensile Modulus | 3.50 GPa | 508 ksi | DIN EN ISO 527 | ||
| Flexural Strength | 110 MPa | 16000 psi | Outer Fiber Stress at 3.5% Outer Fiber Strain; DIN EN ISO 178 | ||
| 127 MPa | 18400 psi | DIN EN ISO 178 | |||
| Flexural Modulus | 3.90 GPa | 566 ksi | DIN EN ISO 178 | ||
| Compressive Yield Strength | 103 MPa | 14900 psi | DIN EN ISO 604 | ||
| Compressive Strength | 76.0 MPa | 11000 psi | Elastic Limit | ||
| 103 MPa | 14900 psi | DIN EN ISO 604 | |||
| 35.0 MPa @Time 3.60e+7 sec | 5080 psi @Time 10000 hour | ||||
| 67.0 MPa @Time 360000 sec | 9720 psi @Time 100 hour | ||||
| 81.0 MPa @Time 36.0 sec | 11700 psi @Time 0.0100 hour | ||||
| 80.0 MPa @Strain 3.50 % | 11600 psi @Strain 3.50 % | DIN EN ISO 604 | |||
| Compressive Modulus | 2.54 GPa | 368 ksi | DIN EN ISO 604 | ||
| Fatigue Strength | 56.0 MPa @Frequency 1.00 Hz, Temperature 20.0 °C | 8120 psi @Frequency 1.00 Hz, Temperature 68.0 °F | 10° stress cycles | ||
| K Factor (ISO) | 1.4 µm/km @Temperature 100 °C | 1.4 µm/km @Temperature 212 °F | |||
| 4.8 µm/km @Temperature 200 °C | 4.8 µm/km @Temperature 392 °F | ||||
| 6.4 µm/km @Temperature 240 °C | 6.4 µm/km @Temperature 464 °F | ||||
| 12.1 µm/km @Temperature 20.0 °C | 12.1 µm/km @Temperature 68.0 °F | ||||
| Charpy Impact Unnotched | NB | NB | EN ISO 179/1eU | ||
| Charpy Impact, Notched | 0.630 J/cm² | 3.00 ft-lb/in² | EN ISO 179/1eA | ||
| Coefficient of Friction, Dynamic | 0.090 @Temperature 100 °C | 0.090 @Temperature 212 °F | Dry Operation | ||
| 0.16 @Temperature 20.0 °C | 0.16 @Temperature 68.0 °F | Dry Operation | |||
| Coefficient of Friction, Static | 0.13 @Temperature 20.0 °C | 0.13 @Temperature 68.0 °F | Dry Operation | ||
| Tensile Creep Modulus, 1000 hours | 2500 MPa | 363000 psi | At 1% Deformation; DIN 53444 | ||
| Limiting Pressure Velocity | 0.46666 MPa-m/sec | 13323 psi-ft/min | v = 100m/min | ||
| 0.500 MPa-m/sec | 14300 psi-ft/min | v = 200m/min | |||
| 0.66666 MPa-m/sec | 19033 psi-ft/min | v = 10m/min | |||
| 1.0355 MPa-m/sec | 29564 psi-ft/min | v = 1m/min | |||
| Compression Set | 3.3 % | 3.3 % | Elastic Compression Limit | ||
| 5.4 % | 5.4 % | Nominal Compressive Yield Strain; DIN EN ISO 604 | |||
| 5.4 % | 5.4 % | Nominal Compressive Strain at Compressive Strength; DIN EN ISO 604 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 6.00e+16 ohm-cm | 6.00e+16 ohm-cm | IEC 93 | ||
| Surface Resistance | 6.80e+12 ohm | 6.80e+12 ohm | IEC 93 | ||
| Dielectric Constant | 3.3 @Frequency 110 Hz | 3.3 @Frequency 110 Hz | IEC 250 | ||
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | IEC 243 | ||
| Dissipation Factor | 0.0020 | 0.0020 | IEC 112 | ||
| 0.061 @Frequency 1.00 Hz | 0.061 @Frequency 1.00 Hz | ||||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 62.0 µm/m-°C @Temperature <=100 °C | 34.4 µin/in-°F @Temperature <=212 °F | ISO E 830 | ||
| 65.0 µm/m-°C @Temperature <=150 °C | 36.1 µin/in-°F @Temperature <=302 °F | ISO E 831 | |||
| Specific Heat Capacity | 1.05 J/g-°C | 0.251 BTU/lb-°F | DSC | ||
| Melting Point | 340 °C | 644 °F | DSC | ||
| Maximum Service Temperature, Air | 115 °C | 239 °F | Pressed Bushings | ||
| 250 °C | 482 °F | Continuous | |||
| 260 °C | 500 °F | Short Term (3h) | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 171 °C | 340 °F | DIN EN ISO 75 | ||
| Glass Transition Temp, Tg | 146 °C | 295 °F | DSC | ||
| Flammability, UL94 | V-0 | V-0 | |||
| Descriptive Properties | |||||
| Alignment Adjustment | 4 | Nominal Scale: 1, low; 10, high | |||
| Chemical Sterilization | 10 | Nominal Scale: 1, low; 10, high | |||
| Color | Beige | ||||
| Creep Resistance | 5 | Nominal Scale: 1, low; 10, high | |||
| Dimensional Stability with Thermal Expansion | 5 | Nominal Scale: 1, low; 10, high | |||
| FDA Compliant | Applicable | ||||
| Free from Silicon | Applicable | ||||
| Gamma-rays Radiation Sterilization | 7 | Nominal Scale: 1, low; 10, high | |||
| High Precision Bushings (negative clearance) | Applicable | ||||
| Injection Molded Parts | Applicable | ||||
| Machined Parts | Applicable | ||||
| Moist Heat Sterilization | 10 | Nominal Scale: 1, low; 10, high | |||
| Plastic Granules | Applicable | ||||
| Resistance Against dust, Dirt, Abrasive Substances | 7 | Nominal Scale: 1, low; 10, high | |||
| Resistance Against Hot Water | 200 | ||||
| Resistance to Chemicals | 9 | Nominal Scale: 1, low; 10, high | |||
| Resistant Against Disinfectant | Applicable | ||||
| Rods up to Øe (de) | Applicable | ||||
| ROHS/WEEE | Applicable | ||||
| Sheets up to Maximum Thickness | Applicable | ||||
| Sliding Velocity | 200 | ||||
| Suitable for Outdoor Use | 7 | Nominal Scale: 1, low; 10, high | |||
| Suitable for Use in Water | Applicable | ||||
| Suitable for Vacuum | Applicable | ||||
| Tubes (hollow rods) up to Øe (de) | Applicable | ||||
| UV Rays Resistance | 9 | Nominal Scale: 1, low; 10, high | |||
| UV-Sterilization | 7 | Nominal Scale: 1, low; 10, high | |||