- 弯曲强度 [MPa]: 7.58
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | silicone property; Arlon SQA-TMS-024 | ||
| Thickness | 25.4 microns | 1.00 mil | laminated film; Arlon SQA-TMS-003 | ||
| 25.4 microns | 1.00 mil | side 2 layer 2; Arlon SQA-TMS-003 | |||
| 31.8 microns | 1.25 mil | side 2 layer 3; Arlon SQA-TMS-003 | |||
| 31.8 microns | 1.25 mil | side 2 layer 1; Arlon SQA-TMS-003 | |||
| 63.5 microns | 2.50 mil | side 1; Arlon SQA-TMS-003 | |||
| 203 microns | 8.00 mil | substrate; Arlon SQA-TMS-003 | |||
| 381 microns | 15.0 mil | overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 44 | 44 | silicone property; ASTM D2240 | ||
| Tensile Strength, Ultimate | 7.58 MPa | 1100 psi | silicone property; ASTM D412 | ||
| Elongation at Break | 650 % | 650 % | silicone property; ASTM D412 | ||
| Adhesive Bond Strength | 0.0103 MPa | 1.50 psi | adhesion to Al initially; Arlon SQA-TMS-011 | ||
| 0.0172 MPa | 2.50 psi | adhesion to Al at 24 hours; Arlon SQA-TMS-011 | |||
| 0.0276 MPa | 4.00 psi | adhesion to Al at 72 hours; Arlon SQA-TMS-011 | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 160 °C | 320 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Shelf Life | 12.0 Month @Temperature 23.9 °C | 12.0 Month @Temperature 75.0 °F | |||
| Descriptive Properties | |||||
| Color | Silver | ||||