BASF PA66 1000-11 NF2001_产品资讯

BASF PA66 1000-11 NF2001 化学式：[-NH（CH2）6－NHCO(CH2)4CO]n－能耐酸、碱、大多数无机盐水溶液、卤代烷、烃类、酯类、酮类等腐蚀。

物性表：

Physical Properties	Metric	English	Comments

Density	1.14 g/cc	0.0412 lb/in³	ISO 1183
Water Absorption	8.5 %	8.5 %	ISO 62
Moisture Absorption at Equilibrium	2.5 %	2.5 %	23°C/50% R.H.; ISO 62
Linear Mold Shrinkage	0.016 cm/cm	0.016 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	83.0 MPa	12000 psi	2 in/min; ASTM Test
	83.0 MPa	12000 psi	50mm/min; ISO 527
Elongation at Break	25 %	25 %	50mm/min, Nominal strain; ISO 527
	60 %	60 %	2 in/min; ASTM Test
Elongation at Yield	5.0 %	5.0 %	50mm/min; ISO 527
Tensile Modulus	3.00 GPa	435 ksi	1mm/min; ISO 527
Flexural Strength	117 MPa	17000 psi	ASTM Test
Flexural Modulus	2.80 GPa	406 ksi	ISO Data
	2.90 GPa	421 ksi	ASTM Test
Izod Impact, Notched	0.530 J/cm @Thickness 3.17 mm	0.993 ft-lb/in @Thickness 0.125 in	ASTM Test
Izod Impact, Notched (ISO)	5.20 kJ/m²	2.47 ft-lb/in²	ISO Test
Charpy Impact Unnotched	NB	NB	ISO 179
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 179
Charpy Impact, Notched	0.570 J/cm²	2.71 ft-lb/in²	ISO 179
	0.400 J/cm² @Temperature -30.0 °C	1.90 ft-lb/in² @Temperature -22.0 °F	ISO 179

Thermal Properties	Metric	English	Comments
Melting Point	257 °C	495 °F	10 K/min
	257 °C	495 °F	ASTM Test
Deflection Temperature at 0.46 MPa (66 psi)	205 °C	401 °F	ISO 75
	243 °C	469 °F	ASTM Test
Deflection Temperature at 1.8 MPa (264 psi)	72.0 °C	162 °F	ISO 75
	77.0 °C	171 °F	ASTM Test

Descriptive Properties
Color	Natural
Commercial Status	Active America
Impact Modified	No
Primary Processing Technique	Injection Molding

上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。

PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。

欢迎各位客户前来咨询：

联系人：夏先生

手机：13501802636

QQ ：205730283

邮箱：205730283@qq.com

图样：

物理化学性：PA66塑胶原料为半透明或不透明乳白包或带黄色颗粒状结晶形聚合物，具有可塑性。密度（g/cm3） 1．10-1．14；拉伸强度(MPa) 60. 0-80．0；洛氏硬度118；熔点252℃；脆化温度-30℃；热分解温度大于350℃；连续耐热80-120℃；冲击强度（kJ/m2） 60-100；静弯曲强度(MPa) 1 00-120；马丁耐热(℃) 50-60；弯曲弹性模量 (MPa) 2000～3000；体积电阻率（Ωcm） 1.83×1015；平衡吸水率2．5%；介电常数 1．63。