| 物性表： | |||||
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 | ||
| Water Absorption | 8.0 - 9.0 % | 8.0 - 9.0 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.6 - 3.2 % | 2.6 - 3.2 % | (23°C/50% R.H.); ISO 62 | ||
| Viscosity Test | 150 cm³/g | 150 cm³/g | Viscosity number; ISO 307 | ||
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | |||
| Melt Flow | 162 g/10 min @Load 5.00 kg, Temperature 275 °C |
162 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | 50mm/min; ISO 527 | ||
| Elongation at Yield | 20 % | 20 % | 50mm/min; ISO 527 | ||
| Modulus of Elasticity | 1.50 GPa | 218 ksi | ISO 527 | ||
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | ISO 180/A | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| Charpy Impact, Notched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179/1eA | ||
| Tensile Creep Modulus, 1000 hours | 890 MPa | 129000 psi | ISO 899 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+9 ohm-cm | 1.00e+9 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 | ||
| Dielectric Constant | 6.0 @Frequency 1.00e+6 Hz |
6.0 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| Dissipation Factor | 0.30 @Frequency 1.00e+6 Hz |
0.30 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| Comparative Tracking Index | 600 V | 600 V | Test Solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Specific Heat Capacity | 1.70 J/g-°C | 0.406 BTU/lb-°F | |||
| Thermal Conductivity | 0.330 W/m-K | 2.29 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 243 °C | 469 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 107 °C | 225 °F | for 50% loss of tensile strength after 20,000 hr | ||
| 123 °C | 253 °F | for 50% loss of tensile strength after 5,000 hr | |||
| 200 °C | 392 °F | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | Injection-molding/Extrusion | ||
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Injection-molding | ||
| De |
|||||
| Color | Natural | ||||
| Commercial Status | North America and Europe | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
材料的密度1.30-1.40g/cm^3 一、性能指标: 外观 微黄色均匀颗粒 相对密度 1.30～1.40 含湿量(%) ≤1.5 拉伸强度(MPa) ≥150 静弯曲强度(MPa) ≥220 弯曲弹性模量(MPa) ≥6.5×103 缺口冲击强度(KJ/m2) ≥15 热变形温度(1.81MPa，℃) ≥210 玻璃纤维含量(%) 30±2 二、用途 本产品居于高强度、高耐热性、热胀系数和收缩率小，吸水性低，尺寸稳定性随大气湿度和温度变化而不大，它适合制作凸轮、伐座、收音机零部件、电子仪表零件、汽车交通零部件等。