密度0.980克/立方厘米0.0354磅/立方英寸熔体
1.15克/立方厘米0.0415磅/立方英寸
吸水率0.40％0.40％
吸湿在均衡0.20％0.20％23℃/ 50％RH下
熔体流动19克/ 10分钟
@Load2.16千克，
温度330°C 19克/ 10分钟
@Load4.76磅，
温度626°F
力学性能公制英语评论
抗拉强度，屈服65.0兆帕9430 PSI
断裂伸长率> = 50％> = 50％，名义断裂伸长率
屈服伸长率7.0％7.0％
拉伸模量2.30 GPA 334 KSI
简支梁冲击无缺口NB NB
NB
@Temperature -30.0℃，NB
@Temperature -22.0°F
夏比冲击，缺口0.800焦耳/平方厘米3.81英尺 - 磅/平方英寸
0.800焦耳/平方厘米
@Temperature -30.0℃，3.81英尺磅/平方英寸
@Temperature -22.0°F
电气性能公制英语评论
体积电阻率> = 1.00E + 13欧姆厘米> = 1.00E + 13欧姆厘米
表面电阻> = 1.00E + 15欧姆> = 1.00E + 15欧姆
介电常数3.0
@Frequency 100赫兹3.0
@Frequency 100赫兹
3.0
@Frequency 1E + 6赫兹3.0
@Frequency 1E + 6赫兹
介电强度35.0千伏/毫米889千伏/中
耗散因数0.0020
@Frequency 100赫兹0.0020
@Frequency 100赫兹
0.0080
@Frequency 1E + 6赫兹0.0080
@Frequency 1E + 6赫兹
漏电起痕指数600 V 600 V
热性能公制英语评论
CTE，直线，平行流动70.0微米/ M-℃，
@Temperature 20.0℃，38.9μ英寸/ IN-°F
@Temperature 68.0°F
CTE，线性的，横向流量70.0微米/ M-℃，
@Temperature 20.0℃，38.9μ英寸/ IN-°F
@Temperature 68.0°F
比热容1.70焦耳/ G-℃，0.406 BTU / LB-°F熔体
热导率0.167 W / mK的1.16 BTU-IN / HR-ft²-°F熔体
在0.46兆帕变形温度（66 psi）的173℃，343°F
热变形温度在1.8兆帕（264磅），158℃，316°F
维卡软化点181℃，358°F 50℃/ h的50N
易燃性，UL94 HB
@Thickness1.50毫米HB
@Thickness在0.0591
HB
@Thickness3.00毫米HB
@Thickness 0.118的
氧指数24％24％
光学性质公制英语评论
传输，可见80％80％制造商指出透明但不量化
加工性能公制英语评论
熔体温度330℃，626°F注塑
模具温度100℃，212°F注塑
脱模温度163℃，325°F
注射速度为200mm /秒7.87英寸/秒
描述属性
有效的热扩散0.1E-6平方米/ s的熔体.............................................
德国拜耳物性表
生产厂家：德国拜耳
生产型号 PC DP1-9359/5
生产分类：聚合物;热塑性;聚碳酸酯（PC）;聚碳酸酯，模压
德国拜耳 PC DP1-9359/5原材料外包装图：
德国拜耳 PC DP1-9359/5原材料内颗粒图：
材质注：主要特点：
脱模剂
未填
合适的处理方法：
注塑
热成型
针对PC的缺点对其改性增强 PC密度在1.2%以上
》与其它材料合金
》PC加工困难，易粘模，加脱模剂，使它不粘模 R，
》阻燃增强V 阻燃等级
》PC不耐候，不耐紫外，对其添加UV剂，抗紫外
》玻璃纤维增强GF，提高强度，耐热温度
》铁氟龙PTFE增强L，耐磨，耐化学性好
》碳纤维增强 导电，电磁屏蔽（EMI)
PC塑胶原料性能优越，有阻燃级、抗UV级、食品级、玻纤增强级、高韧性、光学级、耐化学性、耐寒性、医用级、
可接触日常餐具、化学器皿、婴幼儿奶瓶、超薄制品、电器外壳、导电产品、电源支架、寿命性佳。
生产品牌有：三菱工程PC、出光PC、拜耳PC、奇美PC、陶氏PC、三星PC、住友化学PC、帝人PC等。
PC塑胶原料主要应用于：
1、汽车： 保险杆、分电盘、安全玻璃。
2、电子电器：家电外壳、CD片、信号筒、开关、电话机。
3、工业零件：照相机本体、潜水镜、机具外壳、安全帽、安全镜片。
4、其它方面：建筑上用作中空筋双壁板、暖房玻璃等；在纺织行业用作纺织纱管、纺织机轴瓦等；
物性表
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.980 g/cc | 0.0354 lb/in³ | Melt | ||
| 1.15 g/cc | 0.0415 lb/in³ | ||||
| Water Absorption | 0.40 % | 0.40 % | |||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H. | ||
| Melt Flow | 19 g/10 min @Load 2.16 kg, Temperature 330 °C |
19 g/10 min @Load 4.76 lb, Temperature 626 °F |
|||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | |||
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain at Break | ||
| Elongation at Yield | 7.0 % | 7.0 % | |||
| Tensile Modulus | 2.30 GPa | 334 ksi | |||
| Charpy Impact Unnotched | NB | NB | |||
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
||||
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | |||
| 0.800 J/cm² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
||||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | |||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |||
| Dielectric Constant | 3.0 @Frequency 100 Hz |
3.0 @Frequency 100 Hz |
|||
| 3.0 @Frequency 1e+6 Hz |
3.0 @Frequency 1e+6 Hz |
||||
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | |||
| Dissipation Factor | 0.0020 @Frequency 100 Hz |
0.0020 @Frequency 100 Hz |
|||
| 0.0080 @Frequency 1e+6 Hz |
0.0080 @Frequency 1e+6 Hz |
||||
| Comparative Tracking Index | 600 V | 600 V | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature 20.0 °C |
38.9 µin/in-°F @Temperature 68.0 °F |
|||
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature 20.0 °C |
38.9 µin/in-°F @Temperature 68.0 °F |
|||
| Specific Heat Capacity | 1.70 J/g-°C | 0.406 BTU/lb-°F | Melt | ||
| Thermal Conductivity | 0.167 W/m-K | 1.16 BTU-in/hr-ft²-°F | Melt | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 173 °C | 343 °F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | |||
| Vicat Softening Point | 181 °C | 358 °F | 50°C/h 50N | ||
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
|||
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
||||
| Oxygen Index | 24 % | 24 % | |||
| Optical Properties | Metric | English | Comments | ||
| Transmission, Visible | 80 % | 80 % | Manufacturer states transparent but does not quantify | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 330 °C | 626 °F | Injection Molding | ||
| Mold Temperature | 100 °C | 212 °F | Injection Molding | ||
| Ejection Temperature | 163 °C | 325 °F | |||
| Injection Velocity | 200 mm/sec | 7.87 in/sec | |||
| De |
|||||
| Effective thermal diffusivity | 0.1E-6 m²/s | Melt | |||