PA66 70G13HS1L NC010 具自熄性

PA66 70G13HS1L NC010 透明或不透明乳白色结晶形聚合物，PA66 70G13HS1L NC010 具有可塑性。密度1．15g/cm3。熔点252℃。脆化温度-30℃。热分解温度大于350℃。 PA66 70G13HS1L NC010 连续耐热80-120℃,平衡吸水率2．5%。能耐酸、碱、大多数无机盐水溶液、卤代烷、烃类、酯类、酮类等腐蚀。
 PA66 70G13HS1L NC010 PA66在较高温度也能保持较强的强度和刚度。PA66在成型后仍然具有吸湿性，其程度主要取决于材料的组成、壁厚以及环境条件。
 物性表：
Physical Properties Metric English Comments
Density  1.23 g/cc 0.0444 lb/in³ DAM; ISO 1183
Water Absorption  7.6 %
@Thickness 2.00 mm		 7.6 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Moisture Absorption  2.20 %
@Thickness 2.00 mm		 2.20 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Water Absorption at Saturation  1.7 % 1.7 % DAM; Immersion 24h; ASTM D570
Viscosity Test  150 cm³/g 150 cm³/g DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow  0.0070 cm/cm 0.0070 in/in DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.012 cm/cm 0.012 in/in DAM; ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  75.0 MPa 10900 psi 50%RH; ISO 527-1/-2
  120 MPa 17400 psi DAM; ISO 527-1/-2
Tensile Stress    15.93 MPa
@Strain 0.270 %,
Temperature 23.0 °C		 2310 psi
@Strain 0.270 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  16.9 MPa
@Strain 0.250 %,
Temperature -40.0 °C		 2450 psi
@Strain 0.250 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  58.34 MPa
@Strain 1.08 %,
Temperature 23.0 °C		 8462 psi
@Strain 1.08 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  58.9 MPa
@Strain 1.00 %,
Temperature -40.0 °C		 8540 psi
@Strain 1.00 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  93.71 MPa
@Strain 1.89 %,
Temperature 23.0 °C		 13590 psi
@Strain 1.89 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  96.35 MPa
@Strain 1.75 %,
Temperature -40.0 °C		 13970 psi
@Strain 1.75 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  120 MPa
@Strain 2.70 %,
Temperature 23.0 °C		 17400 psi
@Strain 2.70 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  128.5 MPa
@Strain 2.50 %,
Temperature -40.0 °C		 18640 psi
@Strain 2.50 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
Elongation at Break  3.0 % 3.0 % DAM; ISO 527-1/-2
  13 % 13 % 50%RH; ISO 527-1/-2
Tensile Modulus  3.50 GPa 508 ksi 50%RH; ISO 527-1/-2
  5.50 GPa 798 ksi DAM; ISO 527-1/-2
Flexural Strength  100 MPa 14500 psi 50%RH; ISO 178
  190 MPa 27600 psi DAM; ISO 178
Flexural Modulus  2.90 GPa 421 ksi 50%RH; ISO 178
  4.90 GPa 711 ksi DAM; ISO 178
Secant Modulus    0.845588 GPa
@Strain 6.80 %,
Temperature 100 °C		 122.644 ksi
@Strain 6.80 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  1.03906 GPa
@Strain 6.40 %,
Temperature 80.0 °C		 150.705 ksi
@Strain 6.40 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  1.37353 GPa
@Strain 3.40 %,
Temperature 100 °C		 199.217 ksi
@Strain 3.40 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  1.63438 GPa
@Strain 3.20 %,
Temperature 80.0 °C		 237.050 ksi
@Strain 3.20 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  1.74118 GPa
@Strain 0.850 %,
Temperature 100 °C		 252.541 ksi
@Strain 0.850 %,
Temperature 212 °F		 DAM; ISO 11403-1 -2
  2.2125 GPa
@Strain 0.800 %,
Temperature 80.0 °C		 320.90 ksi
@Strain 0.800 %,
Temperature 176 °F		 DAM; ISO 11403-1 -2
  4.8037 GPa
@Strain 2.16 %,
Temperature 23.0 °C		 696.73 ksi
@Strain 2.16 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  5.39 GPa
@Strain 2.00 %,
Temperature -40.0 °C		 782 ksi
@Strain 2.00 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  5.40185 GPa
@Strain 1.08 %,
Temperature 23.0 °C		 783.484 ksi
@Strain 1.08 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  5.89 GPa
@Strain 1.00 %,
Temperature -40.0 °C		 854 ksi
@Strain 1.00 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  5.90 GPa
@Strain 0.270 %,
Temperature 23.0 °C		 856 ksi
@Strain 0.270 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  6.76 GPa
@Strain 0.250 %,
Temperature -40.0 °C		 980 ksi
@Strain 0.250 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
Izod Impact, Notched (ISO)  4.00 kJ/m² 1.90 ft-lb/in² 50%RH; ISO 180/1A
  4.50 kJ/m² 2.14 ft-lb/in² DAM; ISO 180/1A
   3.00 kJ/m²
@Temperature -40.0 °C		 1.43 ft-lb/in²
@Temperature -40.0 °F		 50%RH; ISO 180/1A
  3.00 kJ/m²
@Temperature -30.0 °C		 1.43 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 180/1A
  4.50 kJ/m²
@Temperature -40.0 °C		 2.14 ft-lb/in²
@Temperature -40.0 °F		 DAM; ISO 180/1A
  4.50 kJ/m²
@Temperature -30.0 °C		 2.14 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 180/1A
Izod Impact, Unnotched (ISO)  40.0 kJ/m² 19.0 ft-lb/in² DAM; ISO 180/1U
  55.0 kJ/m² 26.2 ft-lb/in² 50%RH; ISO 180/1U
   28.0 kJ/m²
@Temperature -30.0 °C		 13.3 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 180/1U
  35.0 kJ/m²
@Temperature -30.0 °C		 16.7 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 180/1U
Charpy Impact Unnotched  3.20 J/cm² 15.2 ft-lb/in² DAM; ISO 179/1eU
  7.00 J/cm² 33.3 ft-lb/in² 50%RH; ISO 179/1eU
   3.00 J/cm²
@Temperature -30.0 °C		 14.3 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eU
  3.00 J/cm²
@Temperature -30.0 °C		 14.3 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eU
Charpy Impact, Notched  0.500 J/cm² 2.38 ft-lb/in² DAM; ISO 179/1eA
  0.600 J/cm² 2.86 ft-lb/in² 50%RH; ISO 179/1eA
   0.400 J/cm²
@Temperature -30.0 °C		 1.90 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eA
  0.450 J/cm²
@Temperature -40.0 °C		 2.14 ft-lb/in²
@Temperature -40.0 °F		 DAM; ISO 179/1eA
Tensile Creep Modulus, 1 hour  3300 MPa
@Time 3600 sec		 479000 psi
@Time 1.00 hour		 50%RH; ISO 899-1
Tensile Creep Modulus, 1000 hours  2200 MPa
@Time 3.60e+6 sec		 319000 psi
@Time 1000 hour		 50%RH; ISO 899-1
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm DAM; IEC 60093
Dissipation Factor    0.0070
@Frequency 1.00e+6 Hz		 0.0070
@Frequency 1.00e+6 Hz		 DAM; IEC 60250
  0.0070
@Frequency 100 Hz		 0.0070
@Frequency 100 Hz		 DAM; IEC 60250
  0.24
@Frequency 100 Hz		 0.24
@Frequency 100 Hz		 50%RH; IEC 60250
  0.24
@Frequency 1.00e+6 Hz		 0.24
@Frequency 1.00e+6 Hz		 50%RH; IEC 60250
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  40.0 µm/m-°C 22.2 µin/in-°F DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  96.0 µm/m-°C 53.3 µin/in-°F DAM; ISO 11359-1/-2
Specific Heat Capacity  2.37 J/g-°C 0.566 BTU/lb-°F  
Thermal Conductivity  0.160 W/m-K 1.11 BTU-in/hr-ft²-°F of melt
Melting Point  262 °C 504 °F DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  258 °C 496 °F DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  238 °C 460 °F DAM; ISO 75-1/-2
Glass Transition Temp, Tg  80.0 °C 176 °F DAM; 10°C/min; ISO 11357-1/-2
Flammability, UL94    HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 DAM; IEC 60695-11-10
  HB
@Thickness 0.700 mm		 HB
@Thickness 0.0276 in		 DAM; IEC 60695-11-10
 
Descriptive Properties
Additives Lubricants  
  Release agent  
Delivery form Pellets  
Eff. thermal diffusivity 8.50E-08 m²/s  
Part Marking Code >PA66-GF13< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PA66-GF13  
Special characteristics Heat stabilised or stable to heat  
UL recognition UL DAM
 
在产品设计时，一定要考虑吸湿性对几何稳定性的影响。为了提高PA66的机械特性，经常加入各种各样的改性剂。玻璃就是最常见的添加剂，有时为了提高抗冲击性还加入合成橡胶，如EPDM和SBR等。PA66的粘性较低，因此流动性很好（但不如PA6）。这个性质可以用来加工很薄的元件。它的粘度对温度变化很敏感。
颗粒
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生  
手  机：13501802636   
QQ    ：205730283  
邮 箱 ：205730283@qq.com 
 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-25475.html

免责声明: 本文 PA66 70G13HS1L NC010 具自熄性 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络