材质注：Starflam R10002E是一个非填充，无卤素和无红磷的阻燃，聚酰胺66/聚酰胺6注塑树脂（又称R1000Z220EM）
由聚合物技术和服务，北美独家供应商提供的信息。
| 物性表： | |||
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.015 cm/cm | 0.0080 - 0.015 in/in | on Tensile Bar; ISO 294 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 |
| Tensile Modulus | 3.40 GPa | 493 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 105 MPa | 15200 psi | ISO 178 |
| Flexural Modulus | 3.50 GPa | 508 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 60.0 kJ/m² | 28.6 ft-lb/in² | 80x10x4; ISO 180/1U |
| Electrical Properties | Metric | English | Comments |
| Comparative Tracking Index | >= 600 V | >= 600 V | PLC 0 |
| Hot Wire Ignition, HWI | 15 - 30 sec @Thickness 0.800 mm |
15 - 30 sec @Thickness 0.0315 in |
PLC 3 |
| High Amp Arc Ignition, HAI | >= 120 arcs @Thickness 0.800 mm |
>= 120 arcs @Thickness 0.0315 in |
PLC 0 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| UL RTI, Electrical | 65.0 °C @Thickness 0.400 mm |
149 °F @Thickness 0.0157 in |
|
| 120 °C @Thickness 0.800 mm |
248 °F @Thickness 0.0315 in |
||
| 120 °C @Thickness 1.60 mm |
248 °F @Thickness 0.0630 in |
||
| 120 °C @Thickness 3.00 mm |
248 °F @Thickness 0.118 in |
||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.400 mm |
149 °F @Thickness 0.0157 in |
|
| 65.0 °C @Thickness 0.800 mm |
149 °F @Thickness 0.0315 in |
||
| 75.0 °C @Thickness 1.60 mm |
167 °F @Thickness 0.0630 in |
||
| 75.0 °C @Thickness 3.00 mm |
167 °F @Thickness 0.118 in |
||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 0.400 mm |
149 °F @Thickness 0.0157 in |
|
| 85.0 °C @Thickness 0.800 mm |
185 °F @Thickness 0.0315 in |
||
| 85.0 °C @Thickness 1.60 mm |
185 °F @Thickness 0.0630 in |
||
| 85.0 °C @Thickness 3.00 mm |
185 °F @Thickness 0.118 in |
||
| Flammability, UL94 | V-0 @Thickness 0.400 mm |
V-0 @Thickness 0.0157 in |
IEC 60695-11-10 |
| V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
IEC 60695-11-10 | |
| V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
IEC 60695-11-10 | |
| V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
IEC 60695-11-10 | |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 260 - 270 °C | 500 - 518 °F | Zone 1 |
| Middle Barrel Temperature | 265 - 280 °C | 509 - 536 °F | Zone 2 |
| Front Barrel Temperature | 265 - 280 °C | 509 - 536 °F | Zone 3 |
| Melt Temperature | 265 - 280 °C | 509 - 536 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 75.0 - 85.0 °C | 167 - 185 °F | |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |
| Moisture Content | 0.20 % | 0.20 % | |
PA66在较高温度也能保持较强的强度和刚度。PA66在成型后仍然具有吸湿性，其程度主要取决于材料的组成、壁厚以及环境条件。
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。