耐韧、PA66 RF0055E 耐冲击性特优_产品资讯

PA66 RF0055E 的收缩率在1%~2%之间，加入玻璃纤维添加剂可以将收缩率降低到0.2%~1% 。收缩率在流程方向和与流程方向相垂直方向上的相异是较大的。PA66对许多溶剂具有抗溶性，但对酸和其它一些氯化剂的抵抗力较弱。

Physical Properties	Metric	English	Comments
物性表：
Density	1.47 g/cc	0.0531 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Time 86400 sec	0.0010 - 0.0030 in/in @Time 24.0 hour	ISO 294

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	140 MPa	20300 psi	5 mm/min; ISO 527
Elongation at Break	2.0 %	2.0 %	5 mm/min; ISO 527
Tensile Modulus	9.80 GPa	1420 ksi	1 mm/min; ISO 527
Flexural Strength	190 MPa	27600 psi	2 mm/min; ISO 178
Flexural Modulus	8.40 GPa	1220 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	8.00 kJ/m²	3.81 ft-lb/in²	80x10x4; ISO 180/1A
Izod Impact, Unnotched (ISO)	40.0 kJ/m²	19.0 ft-lb/in²	80x10x4; ISO 180/1U

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	250 - 400 V	250 - 400 V	PLC 2

Thermal Properties	Metric	English	Comments
Hot Ball Pressure Test	210 °C @Thickness 3.00 mm	410 °F @Thickness 0.118 in	IEC 60695-10-2
Deflection Temperature at 1.8 MPa (264 psi)	210 °C	410 °F	Flatw 80x10x4, sp=64 mm; ISO 75/Af
UL RTI, Electrical	65.0 °C @Thickness 1.00 mm	149 °F @Thickness 0.0394 in	ALL
	65.0 °C @Thickness 1.20 mm	149 °F @Thickness 0.0472 in	ALL
	65.0 °C @Thickness 1.50 - 1.65 mm	149 °F @Thickness 0.0591 - 0.0650 in	ALL
	65.0 °C @Thickness 3.00 mm	149 °F @Thickness 0.118 in	NC
UL RTI, Mechanical with Impact	65.0 °C @Thickness 1.00 mm	149 °F @Thickness 0.0394 in	ALL
	65.0 °C @Thickness 1.20 mm	149 °F @Thickness 0.0472 in	ALL
	65.0 °C @Thickness 1.50 - 1.65 mm	149 °F @Thickness 0.0591 - 0.0650 in	ALL
	65.0 °C @Thickness 3.00 mm	149 °F @Thickness 0.118 in	NC
UL RTI, Mechanical without Impact	65.0 °C @Thickness 1.00 mm	149 °F @Thickness 0.0394 in	ALL
	65.0 °C @Thickness 1.20 mm	149 °F @Thickness 0.0472 in	ALL
	65.0 °C @Thickness 1.50 - 1.65 mm	149 °F @Thickness 0.0591 - 0.0650 in	ALL
	65.0 °C @Thickness 3.00 mm	149 °F @Thickness 0.118 in	NC
Flammability, UL94	V-1 @Thickness 1.00 mm	V-1 @Thickness 0.0394 in	ALL; IEC 60695-11-10
	V-0 @Thickness 1.20 mm	V-0 @Thickness 0.0472 in	ALL; IEC 60695-11-10
	V-0 @Thickness 1.50 - 1.65 mm	V-0 @Thickness 0.0591 - 0.0650 in	ALL; IEC 60695-11-10
	V-0 @Thickness 3.00 mm	V-0 @Thickness 0.118 in	NC; IEC 60695-11-10
Glow Wire Test	850 °C @Thickness 1.00 mm	1560 °F @Thickness 0.0394 in	Glow-Wire Ignition; IEC 60695-2-13
	850 °C @Thickness 1.50 - 1.65 mm	1560 °F @Thickness 0.0591 - 0.0650 in	Glow-Wire Ignition; IEC 60695-2-13
	850 °C @Thickness 3.00 mm	1560 °F @Thickness 0.118 in	Glow-Wire Ignition; IEC 60695-2-13

Processing Properties	Metric	English	Comments
Rear Barrel Temperature	265 - 275 °C	509 - 527 °F	Zone 1
Middle Barrel Temperature	265 - 275 °C	509 - 527 °F	Zone 2
Front Barrel Temperature	270 - 280 °C	518 - 536 °F	Zone 3
Melt Temperature	270 - 280 °C	518 - 536 °F
Mold Temperature	60.0 - 100 °C	140 - 212 °F
Drying Temperature	80.0 °C	176 °F
Dry Time	4.00 hour	4.00 hour
Moisture Content	0.20 %	0.20 %

熔化温度：260~290℃。对玻璃添加剂的产品为275~280℃。熔化温度应避免高于300℃。模具温度：建议80℃。模具温度将影响结晶度，而结晶度将影响产品的物理特性。对于薄壁塑件，如果使用低于40℃的模具温度，则塑件的结晶度将随着时间而变化，为了保持塑件的几何稳定性，需要进行退火处理。