加纤防火PA、PA66 RF0023E_产品资讯

PA66 RF0023E 类别：聚合物；热塑性；尼龙6；尼龙66；尼龙66 / 6，10%玻璃纤维增强。材料说明：starflam rf0023e是无机阻燃剂，无卤、无磷，玻璃纤维，尼龙66 / 6注射成型（也称为rf1002z230em）

Physical Properties	Metric	English	Comments
物性表：
Density	1.73 g/cc	0.0625 lb/in³	ISO 1183
Water Absorption	0.80 % @Temperature 23.0 °C, Time 86400 sec	0.80 % @Temperature 73.4 °F, Time 24.0 hour	ISO 62-1
Linear Mold Shrinkage, Flow	0.0020 - 0.0050 cm/cm @Time 86400 sec	0.0020 - 0.0050 in/in @Time 24.0 hour	ISO 294

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	94.0 MPa	13600 psi	ISO 527
Elongation at Break	1.5 - 2.5 %	1.5 - 2.5 %	ISO 527
Flexural Strength	132 MPa	19100 psi	ISO 178
Flexural Modulus	7.60 GPa	1100 ksi	ISO 178
Izod Impact, Notched (ISO)	3.00 kJ/m²	1.43 ft-lb/in²	80x10x4; ISO 180/1A
Izod Impact, Unnotched (ISO)	22.0 kJ/m²	10.5 ft-lb/in²	80x10x4; ISO 180/1U

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	600 V	600 V	IEC 60112
Hot Wire Ignition, HWI	>= 120 sec @Thickness 0.860 mm	>= 120 sec @Thickness 0.0339 in	PLC 0
High Amp Arc Ignition, HAI	>= 120 arcs @Thickness 0.860 mm	>= 120 arcs @Thickness 0.0339 in	PLC 0
	>= 120 arcs @Thickness 1.70 mm	>= 120 arcs @Thickness 0.0669 in	PLC 0
	>= 120 arcs @Thickness 3.00 mm	>= 120 arcs @Thickness 0.118 in	PLC 0

Thermal Properties	Metric	English	Comments
Thermal Conductivity	1.00 W/m-K	6.94 BTU-in/hr-ft²-°F	ASTM E1530
Hot Ball Pressure Test	178 °C @Thickness 3.00 mm	352 °F @Thickness 0.118 in	IEC 60695-10-2
Deflection Temperature at 1.8 MPa (264 psi)	178 °C	352 °F	Flatw 80x10x4, sp=64 mm; ISO 75/Af
Vicat Softening Point	202 °C	396 °F	B/120; ISO 306
UL RTI, Electrical	130 °C @Thickness 0.860 mm	266 °F @Thickness 0.0339 in
	130 °C @Thickness 1.70 mm	266 °F @Thickness 0.0669 in
	130 °C @Thickness 3.00 mm	266 °F @Thickness 0.118 in
UL RTI, Mechanical with Impact	105 °C @Thickness 0.860 mm	221 °F @Thickness 0.0339 in
	105 °C @Thickness 1.70 mm	221 °F @Thickness 0.0669 in
	105 °C @Thickness 3.00 mm	221 °F @Thickness 0.118 in
UL RTI, Mechanical without Impact	120 °C @Thickness 0.860 mm	248 °F @Thickness 0.0339 in
	130 °C @Thickness 1.70 mm	266 °F @Thickness 0.0669 in
	140 °C @Thickness 3.00 mm	284 °F @Thickness 0.118 in
Flammability, UL94	V-2 @Thickness 0.860 mm	V-2 @Thickness 0.0339 in	IEC 60695-11-10
	V-0 @Thickness 1.70 mm	V-0 @Thickness 0.0669 in	IEC 60695-11-10
	V-0 @Thickness 3.00 mm	V-0 @Thickness 0.118 in	IEC 60695-11-10

Processing Properties	Metric	English	Comments
Rear Barrel Temperature	270 - 280 °C	518 - 536 °F	Zone 1
Middle Barrel Temperature	275 - 285 °C	527 - 545 °F	Zone 2
Front Barrel Temperature	280 - 300 °C	536 - 572 °F	Zone 3
Melt Temperature	280 - 300 °C	536 - 572 °F
Mold Temperature	60.0 - 90.0 °C	140 - 194 °F
Drying Temperature	80.0 °C	176 °F
Dry Time	4.00 hour	4.00 hour
Moisture Content	0.20 %	0.20 %

PA66在较高温度也能保持较强的强度和刚度。PA66在成型后仍然具有吸湿性，其程度主要取决于材料的组成、壁厚以及环境条件。