耐韧、PA66 AFR450X1 耐冲击性特优

PA66 AFR450X1 的收缩率在1%~2%之间，加入玻璃纤维添加剂可以将收缩率降低到0.2%~1% 。PA66 AFR450X1收缩率在流程方向和与流程方向相垂直方向上的相异是较大的。PA66对许多溶剂具有抗溶性，但对酸和其它一些氯化剂的抵抗力较弱。
 PA66 AFR450X1 广泛应用于机械、仪器仪表、汽车部件、电子电气、铁路、家电、通讯、纺机、体育休闲用品、油管、油箱及一些精密工程制品。
 物性表：
Physical Properties Metric English Comments
Density  1.36 g/cc 0.0491 lb/in³ ISO 1183
Moisture Absorption  1.30 %
@Temperature 23.0 °C		 1.30 %
@Temperature 73.4 °F		 50% RH; ISO 62
Water Absorption at Saturation  6.0 %
@Temperature 23.0 °C		 6.0 %
@Temperature 73.4 °F		 ISO 62-1
Linear Mold Shrinkage, Flow  0.0030 - 0.0050 cm/cm 0.0030 - 0.0050 in/in on Tensile Bar; ISO 294
 
Mechanical Properties Metric English Comments
Hardness, Rockwell L  108 108 ISO 2039-2
Tensile Strength at Break  150 MPa 21800 psi 5 mm/min; ISO 527
Elongation at Break  3.0 % 3.0 % 5 mm/min; ISO 527
Tensile Modulus  8.00 GPa 1160 ksi 1 mm/min; ISO 527
Flexural Strength  210 MPa 30500 psi 2 mm/min; ISO 178
Flexural Modulus  7.50 GPa 1090 ksi 2 mm/min; ISO 178
Izod Impact, Notched (ISO)    8.00 kJ/m²
@Temperature -40.0 °C		 3.81 ft-lb/in²
@Temperature -40.0 °F		 80x10x4; ISO 180/1A
  9.00 kJ/m²
@Temperature -20.0 °C		 4.28 ft-lb/in²
@Temperature -4.00 °F		 80x10x4; ISO 180/1A
  12.0 kJ/m²
@Temperature 23.0 °C		 5.71 ft-lb/in²
@Temperature 73.4 °F		 80x10x4; ISO 180/1A
Charpy Impact Unnotched    5.50 J/cm²
@Temperature -30.0 °C		 26.2 ft-lb/in²
@Temperature -22.0 °F		 Edgew 80x10x4; ISO 179/1eU
  6.50 J/cm²
@Temperature 23.0 °C		 30.9 ft-lb/in²
@Temperature 73.4 °F		 Edgew 80x10x4; ISO 179/1eU
Charpy Impact, Notched    0.800 J/cm²
@Temperature -30.0 °C		 3.81 ft-lb/in²
@Temperature -22.0 °F		 Edgew 80x10x4; ISO 179/1eA
  1.10 J/cm²
@Temperature 23.0 °C		 5.23 ft-lb/in²
@Temperature 73.4 °F		 Edgew 80x10x4; ISO 179/1eA
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm IEC 60093
Surface Resistance  >= 1.00e+15 ohm >= 1.00e+15 ohm ROA; IEC 60093
Dielectric Constant    2.6
@Frequency 1.00e+6 Hz		 2.6
@Frequency 1.00e+6 Hz		 IEC 60250
  2.9
@Frequency 50.0 - 60.0 Hz		 2.9
@Frequency 50.0 - 60.0 Hz		 IEC 60250
Dielectric Strength  16.0 kV/mm
@Thickness 3.20 mm		 406 kV/in
@Thickness 0.126 in		 in oil; IEC 60243-1
Dissipation Factor    0.0049
@Frequency 50.0 - 60.0 Hz		 0.0049
@Frequency 50.0 - 60.0 Hz		 IEC 60250
  0.012
@Frequency 1.00e+6 Hz		 0.012
@Frequency 1.00e+6 Hz		 IEC 60250
Comparative Tracking Index  400 V 400 V M; IEC 60112
  550 V 550 V IEC 60112
Hot Wire Ignition, HWI    30 - 60 sec
@Thickness 0.750 mm		 30 - 60 sec
@Thickness 0.0295 in		 PLC 2
  >= 120 sec
@Thickness 1.50 mm		 >= 120 sec
@Thickness 0.0591 in		 PLC 0
  >= 120 sec
@Thickness 3.00 mm		 >= 120 sec
@Thickness 0.118 in		 PLC 0
High Amp Arc Ignition, HAI    >= 120 arcs
@Thickness 0.750 mm		 >= 120 arcs
@Thickness 0.0295 in		 PLC 0
  >= 120 arcs
@Thickness 1.50 mm		 >= 120 arcs
@Thickness 0.0591 in		 PLC 0
  >= 120 arcs
@Thickness 3.00 mm		 >= 120 arcs
@Thickness 0.118 in		 PLC 0
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  25.0 µm/m-°C
@Temperature 23.0 - 60.0 °C		 13.9 µin/in-°F
@Temperature 73.4 - 140 °F		 ISO 11359-2
CTE, linear, Transverse to Flow  90.0 µm/m-°C
@Temperature 23.0 - 60.0 °C		 50.0 µin/in-°F
@Temperature 73.4 - 140 °F		 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)  250 °C 482 °F Edgew 120x10x4, sp=100 mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi)  230 °C 446 °F Edgew 120x10x4, sp=100 mm; ISO 75/Af
Vicat Softening Point  240 °C 464 °F B/120; ISO 306
  240 °C 464 °F B/50; ISO 306
UL RTI, Electrical    110 °C
@Thickness 0.750 mm		 230 °F
@Thickness 0.0295 in		  
  110 °C
@Thickness 1.50 mm		 230 °F
@Thickness 0.0591 in		  
  110 °C
@Thickness 3.00 mm		 230 °F
@Thickness 0.118 in		  
UL RTI, Mechanical with Impact    110 °C
@Thickness 0.750 mm		 230 °F
@Thickness 0.0295 in		  
  110 °C
@Thickness 1.50 mm		 230 °F
@Thickness 0.0591 in		  
  110 °C
@Thickness 3.00 mm		 230 °F
@Thickness 0.118 in		  
UL RTI, Mechanical without Impact    115 °C
@Thickness 0.750 mm		 239 °F
@Thickness 0.0295 in		  
  115 °C
@Thickness 1.50 mm		 239 °F
@Thickness 0.0591 in		  
  120 °C
@Thickness 3.00 mm		 248 °F
@Thickness 0.118 in		  
Flammability, UL94    V-0
@Thickness 0.750 mm		 V-0
@Thickness 0.0295 in		 IEC 60695-11-10
  V-0
@Thickness 1.50 mm		 V-0
@Thickness 0.0591 in		 IEC 60695-11-10
  V-0
@Thickness 3.00 mm		 V-0
@Thickness 0.118 in		 IEC 60695-11-10
Oxygen Index  28 % 28 % ISO 4589
Glow Wire Test  960 °C
@Thickness 2.00 mm		 1760 °F
@Thickness 0.0787 in		 IEC 60695-2-12
 
Processing Properties Metric English Comments
Rear Barrel Temperature  275 - 285 °C 527 - 545 °F Zone 1
Middle Barrel Temperature  275 - 285 °C 527 - 545 °F Zone 2
Front Barrel Temperature  275 - 285 °C 527 - 545 °F Zone 3
Melt Temperature  275 - 285 °C 527 - 545 °F  
Mold Temperature  70.0 - 90.0 °C 158 - 194 °F  
Drying Temperature  75.0 - 85.0 °C 167 - 185 °F  
Dry Time  4.00 - 6.00 hour 4.00 - 6.00 hour  
Moisture Content  0.10 % 0.10 %  
熔化温度：260~290℃。对玻璃添加剂的产品为275~280℃。熔化温度应避免高于300℃。 模具温度：建议80℃。模具温度将影响结晶度，而结晶度将影响产品的物理特性。对于薄壁塑件，如果使用低于40℃的模具温度，则塑件的结晶度将随着时间而变化，为了保持塑件的几何稳定性，需要进行退火处理。
B颗粒10
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生  
手  机：13501802636   
QQ    ：205730283  
邮 箱 ：205730283@qq.com 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-25708.html

免责声明: 本文 耐韧、PA66 AFR450X1 耐冲击性特优 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4