| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 2.45 g/cc | 0.0885 lb/in³ | |||
| Linear Mold Shrinkage, Flow | 0.00350 - 0.00550 cm/cm | 0.00350 - 0.00550 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.00300 - 0.00500 cm/cm | 0.00300 - 0.00500 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 60.0 MPa | 8700 psi | |||
| Elongation at Break | 0.700 % | 0.700 % | |||
| Tensile Modulus | 9.10 GPa | 1320 ksi | |||
| Charpy Impact Unnotched | 1.50 J/cm² | 7.14 ft-lb/in² | |||
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | |||
| Vicat Softening Point | 170 °C @Load 5.00 kg |
338 °F @Load 11.0 lb |
|||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 240 - 280 °C | 464 - 536 °F | |||
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |||
| Drying Temperature | 90.0 - 100 °C @Time 10800 sec |
194 - 212 °F @Time 3.00 hour |
|||
| De |
|||||
| ISO Shrinkage - Pressure | 60 MPa | ||||
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。