- 密度 [g/cm3]: 0.95
- 拉伸强度 [MPa]: 5.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | ISO 1183 |
| Melt Index of Compound | 3.5 g/10 min @Load 2.16 kg, Temperature 230 °C | 3.5 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 27 | 27 | ISO 608 |
| Tensile Strength at Break | 29.3 MPa | 4250 psi | |
| Tensile Strength, Yield | 5.10 MPa | 740 psi | ASTM D638 |
| Elongation at Break | 550 % | 550 % | ASTM D638 |
| Dart drop Test | 260 g | 0.573 lb | ASTM D1709 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 75.0 °C | 167 °F | DSC |
| Vicat Softening Point | 51.0 °C | 124 °F | ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | 5.2 % | 5.2 % | ASTM D1003 |