- 熔体流动速率 [g/10min]: 8.0
- 密度 [g/cm3]: 0.939
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.939 g/cc | 0.0339 lb/in³ | ASTM D1505, ASTM D1928 Proc A |
| Vinyl Acetate Content | 18 % | 18 % | |
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | ASTM D1238 190/2.16 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 4.40 MPa | 638 psi | ASTM D882 Method A |
| Film Tensile Strength at Yield, TD | 3.70 MPa | 537 psi | ASTM D882 Method A |
| Film Elongation at Break, MD | 475 % | 475 % | ASTM D882 Method A |
| Film Elongation at Break, TD | 653 % | 653 % | ASTM D882 Method A |
| Dart drop Test | 315 g | 0.695 lb | Thickness not specified; ASTM D1709 Method A |
| Film Tensile Strength at Break, MD | 18.7 MPa | 2710 psi | ASTM D882 Method A |
| Film Tensile Strength at Break, TD | 16.7 MPa | 2420 psi | ASTM D882 Method A |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 86.0 °C | 187 °F | ASTM D3417 |
| Vicat Softening Point | 59.0 °C | 138 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 4.9 % | 4.9 % | ASTM D1003 |
| Gloss | 60 % | 60 % | 45° Gloss, ASTM D2457 |