- 熔体流动速率 [g/10min]: 10.0
- 密度 [g/cm3]: 0.93
- 断裂伸长率 [%]: 110
- 弯曲强度 [MPa]: 12.5
- 脆化温度 [℃]: -77.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | ASTM D1505, ASTM D1928 Proc A |
| Vinyl Acetate Content | 9.0 % | 9.0 % | |
| Melt Flow | 10 g/10 min | 10 g/10 min | ASTM D1238 190/2.16 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 95 | 95 | ASTM D2240 |
| Hardness, Shore D | 45 | 45 | ASTM D2240 |
| Tensile Strength, Ultimate | 12.5 MPa | 1810 psi | ASTM D638 Type IV |
| Elongation at Break | 660 % | 660 % | ASTM D638 Type IV |
| Flexural Yield Strength | 110 MPa | 16000 psi | 1% secant, ASTM D790 Method I |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 77.0 °C | 171 °F | ASTM D1525 |
| Brittleness Temperature | -77.0 °C | -107 °F | ASTM D746 |