- 熔体流动速率 [g/10min]: 3.0
- 密度 [g/cm3]: 0.952
- 断裂伸长率 [%]: 17.0
- 弯曲强度 [MPa]: 17.0
- 脆化温度 [℃]: -85.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in³ | ASTM D1505, ASTM D1928 Proc A |
| Vinyl Acetate Content | 28 % | 28 % | |
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ASTM D1238 190/2.16 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 84 | 84 | ASTM D2240 |
| Hardness, Shore D | 30 | 30 | ASTM D2240 |
| Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638 Type IV |
| Elongation at Break | 770 % | 770 % | ASTM D638 Type IV |
| Flexural Yield Strength | 17.0 MPa | 2470 psi | 1% secant, ASTM D790 Method I |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 44.0 °C | 111 °F | ASTM D1525 |
| Brittleness Temperature | <= -85.0 °C | <= -121 °F | ASTM D746 |