- 密度 [g/cm3]: 0.939
- 拉伸强度 [MPa]: 4.8
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.939 g/cc | 0.0339 lb/in³ | ASTM D1505 | ||
| Vinyl Acetate Content | 13 - 15 % | 13 - 15 % | Arkema | ||
| Melt Index of Compound | 9.5 - 11.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 9.5 - 11.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 91 | 91 | ASTM D2240 | ||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ASTM D638 | ||
| 26.0 MPa | 3770 psi | Film Property, 50 µm thickness; ASTM D882 | |||
| Tensile Strength, Yield | 4.80 MPa | 696 psi | ASTM D638 | ||
| 5.60 MPa | 812 psi | Film Property, 50 µm thickness; ASTM D882 | |||
| Elongation at Break | 600 - 900 % | 600 - 900 % | ASTM D638 | ||
| 700 - 900 % | 700 - 900 % | Film Property, 50 µm thickness; ASTM D882 | |||
| Dart drop Test | 180 g | 0.397 lb | ASTM D1709 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 93.0 °C | 199 °F | DSC | ||
| Vicat Softening Point | 66.0 °C | 151 °F | ASTM D1525 | ||
| Ring & Ball Softening Point | 145 °C | 293 °F | |||
| Optical Properties | Metric | English | Comments | ||
| Haze | 3.5 % | 3.5 % | 50 micron film; ASTM D1003 | ||
| Descriptive Properties | |||||
| MAH Mini | 1600 | ||||