- 熔体流动速率 [g/10min]: 9.5
- 密度 [g/cm3]: 0.94
- 拉伸强度 [MPa]: 4.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | ASTM D1505 |
| Vinyl Acetate Content | 13 - 15 % | 13 - 15 % | |
| Melt Flow | 9.5 - 11.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 9.5 - 11.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 32.4 | 32.4 | ISO 868 |
| Tensile Strength at Break | 17.4 MPa | 2520 psi | 50 microns film; ASTM D882 |
| Tensile Strength, Yield | 4.20 MPa | 609 psi | 50 microns film; ASTM D882 |
| Elongation at Break | 650 % | 650 % | 50 microns film; ASTM D882 |
| Modulus of Elasticity | 0.0443 GPa | 6.43 ksi | ISO R527 |
| Dart drop Test | 180 g | 0.397 lb | 50 microns film |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 90.0 °C | 194 °F | D.S.C. method |
| Vicat Softening Point | 62.0 °C | 144 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 5.2 % | 5.2 % | 50 micron film; ASTM D1003 |