- 熔体流动速率 [g/10min]: 2.1
- 密度 [g/cm3]: 0.94
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | ASTM-D1505 | ||
| Vinyl Acetate Content | 19 % | 19 % | |||
| Melt Flow | 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.1 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 89 | 89 | ASTM-D2240 | ||
| Hardness, Shore D | 38 | 38 | ASTM-D2240 | ||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ASTM-D638 | ||
| Elongation at Break | 750 % | 750 % | ASTM-D638 | ||
| Secant Modulus | 0.0330 GPa | 4.79 ksi | 0.05; ASTM-D638 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 86.0 °C | 187 °F | ASTM-D3418 | ||
| Vicat Softening Point | 61.0 °C @Load 1.02 kg | 142 °F @Load 2.25 lb | ASTM-D1525 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Homogenization (Calendering) | ||
| 100 - 120 °C | 212 - 248 °F | Mixing (Bambury) | |||
| 160 - 175 °C | 320 - 347 °F | Pressing | |||
| Descriptive Properties | |||||
| Pressing Pressure (kgf/cm²) | 100 | minimum | |||