- 熔体流动速率 [g/10min]: 2.5
- 密度 [g/cm3]: 0.94
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | D1505 | ||
| Vinyl Acetate Content | 18.5 % | 18.5 % | |||
| Thickness | 31.75 microns | 1.250 mil | Thickness Tested | ||
| Melt Flow | 2.5 g/10 min | 2.5 g/10 min | D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 600 % | 600 % | D882 | ||
| Film Elongation at Break, TD | 800 % | 800 % | D882 | ||
| Dart Drop | 9.13 g/micron | 232 g/mil | D1709 | ||
| Dart drop Test | 290 g | 0.639 lb | D1709 | ||
| Film Tensile Strength at Break, MD | 24.8 MPa | 3600 psi | D638 | ||
| Film Tensile Strength at Break, TD | 24.1 MPa | 3500 psi | D638 | ||
| 1% Secant Modulus, MD | 42.1 MPa | 6110 psi | D882 | ||
| 1% Secant Modulus, TD | 50.3 MPa | 7300 psi | D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 85.0 °C | 185 °F | DSC Peak; D33418 | ||
| Vicat Softening Point | 67.0 °C | 153 °F | D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 3.6 % | 3.6 % | D1003 | ||
| Gloss | 82 % | 82 % | at 45°; D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | <= 177 °C | <= 351 °F | Blown Film | ||
| <= 204 °C | <= 399 °F | Cast Film | |||
| Blow-up Ratio (BUR) | 2.5 | 2.5 | As tested | ||
| Descriptive Properties | |||||
| process | Film | ||||
| region | US & Canada | ||||