- 熔体流动速率 [g/10min]: 8.0
- 密度 [g/cm3]: 0.91
- 拉伸强度 [MPa]: 38.0
- 硬度: 105.0
- 热变形温度 [℃]: 112.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in³ | ISO 1183 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 105 | 105 | ISO 2039-2 |
| Tensile Strength, Yield | 38.0 MPa | 5510 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 7.5 % | 7.5 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 1.80 GPa | 261 ksi | At 1 mm/min; ISO 527-2 |
| Charpy Impact, Notched | 0.550 J/cm² | 2.62 ft-lb/in² | ISO 179/1eA |
| Impact Test | 25.0 J | 18.4 ft-lb | Instrumental Falling Weight - Total Penetration Energy at -20°C; ISO 6603-2 |
| 35.0 J | 25.8 ft-lb | Instrumental Falling Weight - Total Penetration Energy at 0°C; ISO 6603-2 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | ISO 75-2 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 170 - 190 °C | 338 - 374 °F | |
| Die Temperature | 175 - 190 °C | 347 - 374 °F | |