- 熔体流动速率 [g/10min]: 1.6
- 密度 [g/cm3]: 0.9
- 拉伸强度 [MPa]: 25.0
- 弯曲模量 [MPa]: 0.800
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | ISO 1183 |
| Melt Flow | 1.6 g/10 min @Load 2.16 kg, Temperature 230 °C | 1.6 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 63 | 63 | ISO 868 |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Break | <= 200 % | <= 200 % | 50 mm/min; ISO 527-3 |
| Tensile Modulus | 1.40 GPa | 203 ksi | At 1 mm/min; ISO 178 |
| Flexural Modulus | 0.800 GPa | 116 ksi | At 2 mm/min; ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 145 °C | 293 °F | A (10 N); ISO 306 |
| Processing Properties | Metric | English | Comments |
| Front Barrel Temperature | 220 - 240 °C | 428 - 464 °F | |
| Melt Temperature | 225 - 235 °C | 437 - 455 °F | |
| Head Temperature | 220 - 230 °C | 428 - 446 °F | |